Effect of Bond Coats on Thermal Shock Resistance of Thermal Barrier Coatings Deposited Onto Polymer Matrix Composites Via Air Plasma Spray Process
文献类型：期刊论文
| 作者 | Huang, Wenzhi1,2,3; Zhao, Yu2,3; Fan, Xizhi2,3; Meng, Xiangsheng1,3; Wang, Ying2; Cai, Xiaolong2; Cao, Xueqiang2; Wang, Zhen1 |
| 刊名 | JOURNAL OF THERMAL SPRAY TECHNOLOGY
 |
| 出版日期 | 2013-08-01 |
| 卷号 | 22期号:6页码:918-925 |
| 关键词 | Failure Interfaces Polymers X-ray Diffraction |
| ISSN号 | 1059-9630 |
| DOI | 10.1007/s11666-013-9942-7 |
| 英文摘要 | Thermal barrier coating systems with different bond coats were fabricated on polymer matrix composites via the air plasma spray process. During a thermal shock test at 400 A degrees C, Zn and Al interlayers were helpful in improving the thermal shock resistance of coatings due to the low melting point. The coating system consisted of a soft zinc layer as a bond coat, and YSZ as a top coat exhibited the best thermal shock resistance, attributed to the lower residual stress and lower thermal stress in the Zn interlayer. The failure mechanism of the coating system was mainly ascribable to the residual stress derived from the deposition process, thermal stress, and further damage of the substrate. |
| 语种 | 英语 |
| WOS记录号 | WOS:000321869400007 |
| 出版者 | SPRINGER |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/46997]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Huang, Wenzhi |
| 作者单位 | 1.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Jilin, Peoples R China 2.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Rare Earth Resources Utilizat, Changchun 130022, Jilin, Peoples R China 3.Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Huang, Wenzhi,Zhao, Yu,Fan, Xizhi,et al. Effect of Bond Coats on Thermal Shock Resistance of Thermal Barrier Coatings Deposited Onto Polymer Matrix Composites Via Air Plasma Spray Process[J]. JOURNAL OF THERMAL SPRAY TECHNOLOGY,2013,22(6):918-925. |
| APA | Huang, Wenzhi.,Zhao, Yu.,Fan, Xizhi.,Meng, Xiangsheng.,Wang, Ying.,...&Wang, Zhen.(2013).Effect of Bond Coats on Thermal Shock Resistance of Thermal Barrier Coatings Deposited Onto Polymer Matrix Composites Via Air Plasma Spray Process.JOURNAL OF THERMAL SPRAY TECHNOLOGY,22(6),918-925. |
| MLA | Huang, Wenzhi,et al."Effect of Bond Coats on Thermal Shock Resistance of Thermal Barrier Coatings Deposited Onto Polymer Matrix Composites Via Air Plasma Spray Process".JOURNAL OF THERMAL SPRAY TECHNOLOGY 22.6(2013):918-925. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。