Effect of leaving group in dithiocarbamates on mediating melt radical reaction during preparing long chain branched polypropylene
文献类型：期刊论文
| 作者 | Xing, Haiping1,2; Jiang, Zhiwei1,2; Zhang, Zhenjiang1,2; Qiu, Jian1; Wang, Yanhui1; Ma, Li1; Tang, Tao1 |
| 刊名 | POLYMER
 |
| 出版日期 | 2012-02-17 |
| 卷号 | 53期号:4页码:947-955 |
| 关键词 | Branched Melt Polypropylene (Pp) |
| ISSN号 | 0032-3861 |
| DOI | 10.1016/j.polymer.2012.01.004 |
| 英文摘要 | The effectiveness of dithiocarbamates in mediating melt radical reaction during preparing long chain branched polypropylene (LCB-PP) was studied. H-1 NMR, FTIR, GPC-TALLS and rheological measurements were used to characterize the structure of the resultant LCB-PP. The results showed that adding dithiocarbamates could help forming more long chain branches on PP, and furthermore the chemical structure of the leaving group (R) of dithiocarbamates played a key role in adjusting melt reaction of PP in the presence of peroxide and multifunctional monomer. When the R formed a stable radical (compared to PP macroradicals) after leaving from the dithiocarbamate, such as allyl or benzyl radicals, the presence of dithiocarbamates could reduce the chain scission of PP due to the formation of dormant state species. In this case, the polymerization degree of grafted monomer was also reduced comparing with conventional radical polymerization under the same conditions. Thus more multifunctional monomer could react with PP macroradical to form more branching points and then more uniformly distributed LCB structure on the PP backbone. The reaction mechanism was investigated through model reactions. (C) 2012 Elsevier Ltd. All rights reserved. |
| 语种 | 英语 |
| WOS记录号 | WOS:000300525000009 |
| 出版者 | ELSEVIER SCI LTD |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/47827]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Tang, Tao |
| 作者单位 | 1.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
| 推荐引用方式 GB/T 7714 | Xing, Haiping,Jiang, Zhiwei,Zhang, Zhenjiang,et al. Effect of leaving group in dithiocarbamates on mediating melt radical reaction during preparing long chain branched polypropylene[J]. POLYMER,2012,53(4):947-955. |
| APA | Xing, Haiping.,Jiang, Zhiwei.,Zhang, Zhenjiang.,Qiu, Jian.,Wang, Yanhui.,...&Tang, Tao.(2012).Effect of leaving group in dithiocarbamates on mediating melt radical reaction during preparing long chain branched polypropylene.POLYMER,53(4),947-955. |
| MLA | Xing, Haiping,et al."Effect of leaving group in dithiocarbamates on mediating melt radical reaction during preparing long chain branched polypropylene".POLYMER 53.4(2012):947-955. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。