Synthesis of Mg@Mg17Al12 ultrafine particles with superior hydrogen storage properties by hydrogen plasma-metal reaction
文献类型：期刊论文
| 作者 | Liu, Tong1; Qin, Chenggong1; Zhang, Tongwen1; Cao, Yurong1; Zhu, Mu1; Li, Xingguo2 |
| 刊名 | JOURNAL OF MATERIALS CHEMISTRY
 |
| 出版日期 | 2012 |
| 卷号 | 22期号:37页码:19831-19838 |
| ISSN号 | 0959-9428 |
| DOI | 10.1039/c2jm33911k |
| 英文摘要 | In order to improve the hydrogen storage properties of Mg, Mg@Mg17Al12 ultrafine particles (UFPs) with 7, 22 and 27 at% Al have been successfully prepared by a hydrogen plasma-metal reaction (HPMR) approach. These UFPs are nearly spherical in shape with an average size of about 150 nm. The Mg particle core is a single crystal, and the Mg17Al12 particle shell of 2-5 nm thickness effectively suppresses the formation of MgO. The formation mechanism of the core-shell structure is interpreted in terms of Mg-Al phase transformation. The Mg17Al12 shell disproportionates into MgH2 and Al upon hydrogenation, and is recovered after hydrogen release. The morphology and size of these UFPs are not obviously changed during the sorption cycle, whereas the Mg particle core changes from single crystal into the polycrystalline form of 2-4 nm size. The hydrogen sorption kinetics and storage capacity of the Mg@Mg17Al12 UFPs decreased with increasing Al content. Mg-7 at.% Al can absorb 5.7 wt% H-2 at 523 K and 7.0 wt% H-2 at 673 K. It can release 6.0 wt% H-2 within 30 minutes at 623 K and 6.2 wt% H-2 within 3 minutes at 673 K. The catalytic effect and oxidation resistance of the Mg17Al12 shell, and the nanostructure of the Mg core accelerate the hydrogen diffusion, with low hydrogen absorption and desorption activation energies of 49.3 and 105.5 kJ mol(-1), respectively. |
| 语种 | 英语 |
| WOS记录号 | WOS:000308099900062 |
| 出版者 | ROYAL SOC CHEMISTRY |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/49313]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Liu, Tong |
| 作者单位 | 1.Beihang Univ, Sch Mat Sci & Engn, Minist Educ, Key Lab Aerosp Mat & Performance, Beijing 100191, Peoples R China 2.Peking Univ, Coll Chem & Mol Engn, State Key Lab Rare Earth Mat Chem & Applicat, BNLMS, Beijing 100871, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu, Tong,Qin, Chenggong,Zhang, Tongwen,et al. Synthesis of Mg@Mg17Al12 ultrafine particles with superior hydrogen storage properties by hydrogen plasma-metal reaction[J]. JOURNAL OF MATERIALS CHEMISTRY,2012,22(37):19831-19838. |
| APA | Liu, Tong,Qin, Chenggong,Zhang, Tongwen,Cao, Yurong,Zhu, Mu,&Li, Xingguo.(2012).Synthesis of Mg@Mg17Al12 ultrafine particles with superior hydrogen storage properties by hydrogen plasma-metal reaction.JOURNAL OF MATERIALS CHEMISTRY,22(37),19831-19838. |
| MLA | Liu, Tong,et al."Synthesis of Mg@Mg17Al12 ultrafine particles with superior hydrogen storage properties by hydrogen plasma-metal reaction".JOURNAL OF MATERIALS CHEMISTRY 22.37(2012):19831-19838. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。