Fabrication of thermal barrier coatings onto polyimide matrix composites via air plasma spray process
文献类型：期刊论文
| 作者 | Huang, Wenzhi1,2,3; Fan, Xizhi1,3; Zhao, Yu1,3; Zhou, Xin1,3; Meng, Xiangsheng2,3; Wang, Ying1; Zou, Binglin1; Cao, Xueqiang1; Wang, Zhen2 |
| 刊名 | SURFACE & COATINGS TECHNOLOGY
 |
| 出版日期 | 2012-08-25 |
| 卷号 | 207页码:421-429 |
| 关键词 | Air Plasma Spray Thermal Shock Resistance Thermal Ablation Resistance Thermal Stress Failure |
| ISSN号 | 0257-8972 |
| DOI | 10.1016/j.surfcoat.2012.07.042 |
| 英文摘要 | Thermal barrier coatings were fabricated on polyimide matrix composites via air plasma spray process. The phase structures and microstructural evolution of the coatings before and after testing were characterized by powder X-ray diffraction and scanning electron microscopy. During thermal shock test at 400 degrees C, thermal shock lifetime of the coating systems increased with the decrease of thickness of Al layer as well as the increase in that of YSZ layer. The coating system consisted of 30 mu m Al bond layer and 130 mu m YSZ top layer exhibited the best thermal shock resistance. Meanwhile, owing to the protection of the coating system, the weight loss of the sample decreased from 7.05% to 1.90%, while the corresponding mass ablation rate reduced from 0.48 mg s(-1) to 0.21 mg s(-1). Failure mechanism of the coatings was mainly ascribable to the residual stress during deposition, oxidation of substrate and thermal stress induced by mismatch in thermal expansion. Crown Copyright (C) 2012 Published by Elsevier B.V. All rights reserved. |
| 语种 | 英语 |
| WOS记录号 | WOS:000309501600059 |
| 出版者 | ELSEVIER SCIENCE SA |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/49567]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Cao, Xueqiang |
| 作者单位 | 1.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Rare Earth Resources Utilizat, Changchun 130022, Jilin, Peoples R China 2.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Jilin, Peoples R China 3.Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Huang, Wenzhi,Fan, Xizhi,Zhao, Yu,et al. Fabrication of thermal barrier coatings onto polyimide matrix composites via air plasma spray process[J]. SURFACE & COATINGS TECHNOLOGY,2012,207:421-429. |
| APA | Huang, Wenzhi.,Fan, Xizhi.,Zhao, Yu.,Zhou, Xin.,Meng, Xiangsheng.,...&Wang, Zhen.(2012).Fabrication of thermal barrier coatings onto polyimide matrix composites via air plasma spray process.SURFACE & COATINGS TECHNOLOGY,207,421-429. |
| MLA | Huang, Wenzhi,et al."Fabrication of thermal barrier coatings onto polyimide matrix composites via air plasma spray process".SURFACE & COATINGS TECHNOLOGY 207(2012):421-429. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。