Influence of Poly(vinylphenol) Sublayer on the Crystallization Behavior of Poly(3-hydroxybutyrate) Thin Films
文献类型：期刊论文
| 作者 | Sun, Xiaoli1; Chen, Zhen2; Wang, Feng1; Yan, Shouke1; Takahashi, Isao3 |
| 刊名 | MACROMOLECULES
 |
| 出版日期 | 2013-02-26 |
| 卷号 | 46期号:4页码:1573-1581 |
| ISSN号 | 0024-9297 |
| DOI | 10.1021/ma302349a |
| 英文摘要 | The crystallization behavior of poly(3-hydroxybutyrate) (PHB) thin films on poly(vinylphenol) (PVPh) substrate was investigated by surface-sensitive grazing incident X-ray scattering and infrared reflection-absorption spectroscopy techniques. Compared with the crystallization of PHB on a Si wafer, the PVPh sublayer did not significantly affect the crystallization behavior of PHB in solution-cast samples, while significantly inhibited the melt crystallization of PHB. For films thinner than 175 nm, amorphous PHB was always fabricated irrespective of melt crystallization temperature. Only when the film thickness increased to 185 nm, the PHB started to crystallize at temperatures above 53 degrees C. The PHB crystals preferred to orient with the b-axes perpendicular to substrate. The inhibition of PHB melt crystallization was attributed to the thickness confinement and interdiffusion of PVPh and PHB, which caused a concentration gradient of PVPh in the PHB layer. From the thickness dependence of crystallization behavior, the PHB film can be divided into two layers: the inactive layer with high fraction of inter C=O and stable amorphous state; the interactive layer in which crystallization of PHB is sensitive to temperature. The existence of inactive layer accounts for the formation of crystals oriented with b-axes perpendicular to substrate. |
| 语种 | 英语 |
| WOS记录号 | WOS:000315618800036 |
| 出版者 | AMER CHEMICAL SOC |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/54855]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Yan, Shouke |
| 作者单位 | 1.Beijing Univ Chem Technol, State Key Lab Chem Resource Engn, Beijing 100029, Peoples R China 2.Chinese Acad Sci, Inst Chem, State Key Lab Polymer Phys & Chem, Beijing 100080, Peoples R China 3.Kwansei Gakuin Univ, Sch Sci & Technol, Sanda 6691337, Japan |
| 推荐引用方式 GB/T 7714 | Sun, Xiaoli,Chen, Zhen,Wang, Feng,et al. Influence of Poly(vinylphenol) Sublayer on the Crystallization Behavior of Poly(3-hydroxybutyrate) Thin Films[J]. MACROMOLECULES,2013,46(4):1573-1581. |
| APA | Sun, Xiaoli,Chen, Zhen,Wang, Feng,Yan, Shouke,&Takahashi, Isao.(2013).Influence of Poly(vinylphenol) Sublayer on the Crystallization Behavior of Poly(3-hydroxybutyrate) Thin Films.MACROMOLECULES,46(4),1573-1581. |
| MLA | Sun, Xiaoli,et al."Influence of Poly(vinylphenol) Sublayer on the Crystallization Behavior of Poly(3-hydroxybutyrate) Thin Films".MACROMOLECULES 46.4(2013):1573-1581. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。