Structural evolution of tensile-deformed high-density polyethylene during annealing: Scanning synchrotron small-angle X-ray scattering study
文献类型：期刊论文
| 作者 | Jiang, Zhiyong; Tang, Yujing; Men, Yongfeng; Enderle, Hans-Friedrich; Lilge, Dieter; Roth, Stephan V.; Gehrke, Rainer; Rieger, Jens |
| 刊名 | MACROMOLECULES
 |
| 出版日期 | 2007-10-02 |
| 卷号 | 40期号:20页码:7263-7269 |
| ISSN号 | 0024-9297 |
| DOI | 10.1021/ma0627572 |
| 英文摘要 | The structural evolution of high-density polyethylene subjected to uniaxial tensile deformation was investigated as a function of strain and after annealing at different temperatures using a scanning synchrotron small-angle X-ray scattering (SAXS) technique. The results confirm that in the course of tensile deformation intralamellar block slips were activated at small deformations followed by a stress-induced fragmentation and recrystallization process yielding thinner lamellae with their normal parallel to the stretching direction. The original sheared lamellae underwent severe internal deformation so that they were even less stable than the newly developed thinner lamellae. Accordingly, annealing results in a melting of the original crystallites even at moderate strains where the stress-induced fragmentation and recrystallization just sets in and generates a distinctly different form of lamellar stacks aligned along the drawing direction. It was found that the lamellae newly formed during stretching at moderate strains remain stable at lower temperature. Only at a very high annealing temperature of 120 degrees C can they be melted, leading to an isotropic distribution of the lamellar structure. |
| 语种 | 英语 |
| WOS记录号 | WOS:000249845200029 |
| 出版者 | AMER CHEMICAL SOC |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/60959]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Men, Yongfeng |
| 作者单位 | 1.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Grad Sch, Changchun 130022, Peoples R China 2.Basell Polyolefine GmbH, R&D, D-65926 Frankfurt, Germany 3.HASYLAB, D-22607 Hamburg, Germany 4.DESY, D-22607 Hamburg, Germany 5.BASF AG, D-67056 Ludwigshafen, Germany |
| 推荐引用方式 GB/T 7714 | Jiang, Zhiyong,Tang, Yujing,Men, Yongfeng,et al. Structural evolution of tensile-deformed high-density polyethylene during annealing: Scanning synchrotron small-angle X-ray scattering study[J]. MACROMOLECULES,2007,40(20):7263-7269. |
| APA | Jiang, Zhiyong.,Tang, Yujing.,Men, Yongfeng.,Enderle, Hans-Friedrich.,Lilge, Dieter.,...&Rieger, Jens.(2007).Structural evolution of tensile-deformed high-density polyethylene during annealing: Scanning synchrotron small-angle X-ray scattering study.MACROMOLECULES,40(20),7263-7269. |
| MLA | Jiang, Zhiyong,et al."Structural evolution of tensile-deformed high-density polyethylene during annealing: Scanning synchrotron small-angle X-ray scattering study".MACROMOLECULES 40.20(2007):7263-7269. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。