Robust organic/inorganic hybrid porous thin films via breath-figure method and gelation process
文献类型：期刊论文
| 作者 | Zhang, Ke; Zhang, Liwei; Chen, Yongming |
| 刊名 | MACROMOLECULAR RAPID COMMUNICATIONS
 |
| 出版日期 | 2007-10-15 |
| 卷号 | 28期号:20页码:2024-2028 |
| 关键词 | Block Copolymers Organic/inorganic Hybrids Porous Film Sol-gel Process |
| ISSN号 | 1022-1336 |
| 英文摘要 | A novel organic/inorganic hybrid honeycomb patterned porous thin film was prepared using the breath-figure method combined with a sol-gel process. An in situ formed gelable block copolymer, formed by mixing poly(styrene-alt-maleic anliydride)-block-polystyrene (P(St-aMAn)-b-PS) and 3-aminopropyltrimethoxysilane (APS), was used as the structure directing agent. The porous film produced was dipped into an acid aqueous solution to induce a sol-gel process in the wall of film. As a result of gelation, the structure of this film transformed into a crosslinked silica oxide hybridized with PS, and this film resisted those organic solvents which were once good solvents for the copolymer precursor. |
| 语种 | 英语 |
| WOS记录号 | WOS:000250331500009 |
| 出版者 | WILEY-V C H VERLAG GMBH |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/61105]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Chen, Yongming |
| 作者单位 | Chinese Acad Sci, Inst Chem, State Key Lab Polymer Phys & Chem, Joint Lab Polymer Sci & Mat, Beijing 100080, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, Ke,Zhang, Liwei,Chen, Yongming. Robust organic/inorganic hybrid porous thin films via breath-figure method and gelation process[J]. MACROMOLECULAR RAPID COMMUNICATIONS,2007,28(20):2024-2028. |
| APA | Zhang, Ke,Zhang, Liwei,&Chen, Yongming.(2007).Robust organic/inorganic hybrid porous thin films via breath-figure method and gelation process.MACROMOLECULAR RAPID COMMUNICATIONS,28(20),2024-2028. |
| MLA | Zhang, Ke,et al."Robust organic/inorganic hybrid porous thin films via breath-figure method and gelation process".MACROMOLECULAR RAPID COMMUNICATIONS 28.20(2007):2024-2028. |