Synthesis and characterization of polyimide end-capped with fluorinated phenylethynylaniline
文献类型：期刊论文
| 作者 | Chen Jiansheng; Li Zhongxiao; Tao Zhiqiang; Zuo Hongjun; Fan Lin; Yang Shiyong |
| 刊名 | ACTA POLYMERICA SINICA
 |
| 出版日期 | 2007-03-01 |
| 期号 | 3页码:235-239 |
| 关键词 | Fluorinated Phenylethynylaniline Polyimide Pmr Thermal Property |
| ISSN号 | 1000-3304 |
| 英文摘要 | A novel end cap 3-trifluoromethyl-4-(phenylethynyl) aniline (3FPA) was obtained by reduction of the corresponding nitro-compound which was synthesized by coupling of 2-trifluoromethyl-4-nitro-1-bromobenzene with ethynylbenzene.Polyimide monomer solutions were prepared by classic PMR process using p-phenylenediamine (pPDA), the diethyl ester of 4, 4'-hexafluoroisopropylidene-bisphthalic acid (6FDE) and 3-trifluoromethyl-4(phenylethynyl) aniline as endcap. The monomer solution has high solid contents of about 40%-45%, low viscosity of about 28 similar to 36 mPa-s and show high stability at room temperature in two months. The polyimide molding powders were produced by thermally curing the monomer solutions at 200 degrees C, and the imidization degree of powders increased with increasing the curing temperature. The thermosetted polyimides were produced by thermal curing the polyimide molding powders at 370 degrees C under pressure of 1 similar to 2 MPa. The postcured polyimide showed a 5% weight loss temperature of 536 degrees C and Tg about 404 degrees C (DMA) The thermo-oxidative stability of the thermosetted polyimides 3FPA-PI-50 and PMR-II resins at elevated temperature (370 degrees C) were determined by isothermally aging the samples in flowing air atmosphere, and the weight loss of 3FPA-PI-50 was about 6.78 wt% after 300 It isothermal aging which was lower than that of PMR-II (7.15%). |
| 语种 | 英语 |
| WOS记录号 | WOS:000245189900005 |
| 出版者 | SCIENCE CHINA PRESS |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/61207]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Chen Jiansheng |
| 作者单位 | 1.Chinese Acad Sci, Inst Chem, Adv Mat Lab, Beijing 100080, Peoples R China 2.Beijing Inst Graph Commun, Beijing 102600, Peoples R China |
| 推荐引用方式 GB/T 7714 | Chen Jiansheng,Li Zhongxiao,Tao Zhiqiang,et al. Synthesis and characterization of polyimide end-capped with fluorinated phenylethynylaniline[J]. ACTA POLYMERICA SINICA,2007(3):235-239. |
| APA | Chen Jiansheng,Li Zhongxiao,Tao Zhiqiang,Zuo Hongjun,Fan Lin,&Yang Shiyong.(2007).Synthesis and characterization of polyimide end-capped with fluorinated phenylethynylaniline.ACTA POLYMERICA SINICA(3),235-239. |
| MLA | Chen Jiansheng,et al."Synthesis and characterization of polyimide end-capped with fluorinated phenylethynylaniline".ACTA POLYMERICA SINICA .3(2007):235-239. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。