Synthesis and properties of novel sulfonated polyimides containing binaphthyl groups as proton-exchange membranes for fuel cells
文献类型:期刊论文
作者 | Li, Yuhan; Jin, Rizhe; Wang, Zhen; Cui, Zhiming; Xing, Wei; Gao, Lianxun |
刊名 | JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY
![]() |
出版日期 | 2007-01-15 |
卷号 | 45期号:2页码:222-231 |
关键词 | Charge Transport Copolymerization Degree Of Sulfonation Polyimides Proton Conductivity Sulfonated Polyimides 2 2 '-bis(P-aminophenoxy)-1 1 '-binaphthyl-6 6 '-disulfonic Acid |
ISSN号 | 0887-624X |
DOI | 10.1002/pola.21778 |
英文摘要 | A novel sulfonated diamine monomer, 2,2'-bis(p-aminophenoxy)-1,1'-binaphthyl-6,6'-disulfonic acid (BNDADS), was synthesized. A series of sulfonated polyimide copolymers containing 30-80 mol % BNDADS as a hydrophilic component were prepared. The copolymers showed excellent solubility and good film-forming capability. Atomic force microscopy phase images clearly showed hydrophilic/hydrophobic microphase separation. The relationship between the proton conductivity and degree of sulfonation was examined. The sulfonated polyimide copolymer with 60 mol % BNDADS showed higher proton conductivity (0.0945-0.161 S/cm) at 20-80 degrees C in liquid water. The membranes exhibited methanol permeability from 9 x 10(-8) to 5 X 10(-7) cm(2)/s at 20 degrees C, which was much lower than that of Nafion (2 x 10(-6) cm(2)/s). The copolymers were thermally stable up to 300 degrees C. The sulfonated polyimide copolymers with 30-60 mol % BNDADS showed reasonable mechanical strength; for example, the maximum tensile strength at break of the sulfonated polyimide copolymer with 40 mol % BNDADS was 80.6 MPa under high moisture conditions. The optimum concentration of BNDADS was found to be 60 mol % from the viewpoint of proton conductivity, methanol permeability, and membrane stability. (c) 2006 Wiley Periodicals, Inc. |
语种 | 英语 |
WOS记录号 | WOS:000243242700005 |
出版者 | JOHN WILEY & SONS INC |
源URL | [http://ir.iccas.ac.cn/handle/121111/62263] ![]() |
专题 | 中国科学院化学研究所 |
通讯作者 | Gao, Lianxun |
作者单位 | 1.Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100864, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Yuhan,Jin, Rizhe,Wang, Zhen,et al. Synthesis and properties of novel sulfonated polyimides containing binaphthyl groups as proton-exchange membranes for fuel cells[J]. JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY,2007,45(2):222-231. |
APA | Li, Yuhan,Jin, Rizhe,Wang, Zhen,Cui, Zhiming,Xing, Wei,&Gao, Lianxun.(2007).Synthesis and properties of novel sulfonated polyimides containing binaphthyl groups as proton-exchange membranes for fuel cells.JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY,45(2),222-231. |
MLA | Li, Yuhan,et al."Synthesis and properties of novel sulfonated polyimides containing binaphthyl groups as proton-exchange membranes for fuel cells".JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY 45.2(2007):222-231. |
入库方式: OAI收割
来源:化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。