Synthesis and Characterization of Novel Trifunctional Fluorine Containing Epoxy Resins Based on 1,1,1-Tris(2,3-epoxypropoxyphenyl)-2,2,2-trifluoroethane
文献类型：期刊论文
| 作者 | Ge, Ziyi; Tao, Zhiqiang; Liu, Jingang; Fan, Lin; Yang, Shiyong |
| 刊名 | POLYMER JOURNAL
 |
| 出版日期 | 2007 |
| 卷号 | 39期号:11页码:1135-1142 |
| 关键词 | Trifunctional Epoxy Resins Fluorine Containing Polymer Glass Transition Temperature Coefficient Of Thermal Expansion |
| ISSN号 | 0032-3896 |
| DOI | 10.1295/polymj.PJ2007096 |
| 英文摘要 | A novel trifunctional fluorine containing epoxy compound, 1,1,1-Tris(2,3-epoxypropoxyphenyl)-2,2,2-trifluoroethane (TEF) synthesized starting from 4-bromoanisole was cured with alicyclic anhydride or aromatic diamines to produce the epoxy resins. As comparison, commercial available Biphenol A 828 epoxy (BPA) was cured under the same conditions. Experimental results indicated that the cured TEF epoxy resins showed good thermal stability with onset thermal decomposition temperature (T-d) of 363-388 degrees C in nitrogen, glass transition temperature (T-g) of 210-287 degrees C (determined by DMA) and coefficient of thermal expansion (CTE) ranged in 46.7-59.6 ppm/degrees C. The fluorine containing epoxy resins possessed outstanding mechanical properties with flexural strengths of 64-115 MPa, flexural moduli of 2.29-2.65 GPa. The epoxy resins also exhibited excellent electric insulating properties with volume resistivity of 1.19-8.15 x 10(16) Omega.cm and the dielectric constants at 1 MHz of 3.2-3.5 as well as low moisture absorption of 0.31-0.87%. As comparison with BPA resins, the trifunctional fluorine containing TEF resins exhibit higher T, and improved dielectric properties as well as low CTE, which are promising candidates for advanced microelectronic packaging. [doi: 10.1295/polymj.PJ2007096] |
| 语种 | 英语 |
| WOS记录号 | WOS:000207050700009 |
| 出版者 | NATURE PUBLISHING GROUP |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/62633]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Ge, Ziyi |
| 作者单位 | Chinese Acad Sci, Inst Chem, Lab Adv Polymer Mat, Beijing 100080, Peoples R China |
| 推荐引用方式 GB/T 7714 | Ge, Ziyi,Tao, Zhiqiang,Liu, Jingang,et al. Synthesis and Characterization of Novel Trifunctional Fluorine Containing Epoxy Resins Based on 1,1,1-Tris(2,3-epoxypropoxyphenyl)-2,2,2-trifluoroethane[J]. POLYMER JOURNAL,2007,39(11):1135-1142. |
| APA | Ge, Ziyi,Tao, Zhiqiang,Liu, Jingang,Fan, Lin,&Yang, Shiyong.(2007).Synthesis and Characterization of Novel Trifunctional Fluorine Containing Epoxy Resins Based on 1,1,1-Tris(2,3-epoxypropoxyphenyl)-2,2,2-trifluoroethane.POLYMER JOURNAL,39(11),1135-1142. |
| MLA | Ge, Ziyi,et al."Synthesis and Characterization of Novel Trifunctional Fluorine Containing Epoxy Resins Based on 1,1,1-Tris(2,3-epoxypropoxyphenyl)-2,2,2-trifluoroethane".POLYMER JOURNAL 39.11(2007):1135-1142. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。