THE CONTROLLED SYNTHESIS OF POLYANILINE MICROTUBES WITH SQUARE INNER CROSS-SECTION AND POLYAZANE SQUARE MICROBARS
文献类型：期刊论文
| 作者 | Li Jiuming1,2; Zhu Ying2; Xie Qiang1; Wan Meixiang2; Jiang Lei2 |
| 刊名 | ACTA POLYMERICA SINICA
 |
| 出版日期 | 2008-11-20 |
| 期号 | 11页码:1049-1054 |
| ISSN号 | 1000-3304 |
| 关键词 | Polyaniline Polyazane Microtubes With Inner Square Cross-section Microbars With Square Cross-section Self-assembly Process |
| 英文摘要 | Controlled micro/nanostructures of polyaniline (PANI) were obtained through a chemical oxidative polymerization by changing the concentration of aniline monomer in the presence of citric acid as dopant. It was found that conducting PANI microtubes with square inner cross-section (580 similar to 300 nm in diameter and 80 nm in wall thickness) were obtained at a relatively high aniline, concentration. When the solution was sufficiently dilute, the polyazane microbars, with square cross-section (690 similar to 290 nm in side length and 1 similar to 40 mu m in length) can be made by self-assembly. Structural characterizations of the microbars with square cross-section showed that aniline polymerized product by this method was a new material containing N-N single bonds rather than PANI, which was defined as polyazane by A. G. MacDiarmid. The aniline/citric acid salts are proposed as the, templates in the formation of the microtubes with square inner cross-section and microbars with square cross-section based on XRD and SEM measurements. Interestingly, it was found that morphology and molecular Structure of the microbars were strongly affected by the reaction time and the concentration of aniline. The molecular structure of the microbars with square cross-section was changed from polyazane to PANI, for instance, when the reaction time increase from 5 h to 168 h. Moreover,the microbars with square cross-section were varied from solid to hollow with spare cross-section and which was accompanied by a molecular structural change from polyazane, to conductive PANI when the concentration of aniline Increased by one order of magnitude (from 1.75 x 10(-2) to 1.75 x 10(-1) mol/L). |
| 语种 | 英语 |
| 出版者 | SCIENCE CHINA PRESS |
| WOS记录号 | WOS:000260878600005 |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/63407]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Li Jiuming |
| 作者单位 | 1.China Univ Min & Technol, Sch Chem & Environm Engn, Beijing 100083, Peoples R China 2.Chinese Acad Sci, Inst Chem, Ctr Mol Sci, Beijing 100190, Peoples R China |
| 推荐引用方式 GB/T 7714 | Li Jiuming,Zhu Ying,Xie Qiang,et al. THE CONTROLLED SYNTHESIS OF POLYANILINE MICROTUBES WITH SQUARE INNER CROSS-SECTION AND POLYAZANE SQUARE MICROBARS[J]. ACTA POLYMERICA SINICA,2008(11):1049-1054. |
| APA | Li Jiuming,Zhu Ying,Xie Qiang,Wan Meixiang,&Jiang Lei.(2008).THE CONTROLLED SYNTHESIS OF POLYANILINE MICROTUBES WITH SQUARE INNER CROSS-SECTION AND POLYAZANE SQUARE MICROBARS.ACTA POLYMERICA SINICA(11),1049-1054. |
| MLA | Li Jiuming,et al."THE CONTROLLED SYNTHESIS OF POLYANILINE MICROTUBES WITH SQUARE INNER CROSS-SECTION AND POLYAZANE SQUARE MICROBARS".ACTA POLYMERICA SINICA .11(2008):1049-1054. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。