Regio-regular structure high molecular weight poly(propylene carbonate) by rare earth ternary catalyst and Lewis base cocatalyst
文献类型：期刊论文
| 作者 | Tao, Youhua1,2; Wang, Xianhong1; Chen, Xuesi1; Zhao, Xiaojiang1; Wang, Fosong1 |
| 刊名 | JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY
 |
| 出版日期 | 2008-07-01 |
| 卷号 | 46期号:13页码:4451-4458 |
| 关键词 | Biodegradable Carbon Dioxide Copolymerization Lewis Base Polycarbonates Poly(Propylene Carbonate) Regio-regular Stereo-specific Polymers |
| ISSN号 | 0887-624X |
| DOI | 10.1002/pola.22780 |
| 英文摘要 | Lewis base modification strategy on rare earth ternary catalyst was disclosed to enhance nucleophilic ability of active center during copolymerization of carbon dioxide and propylene oxide (PO), poly(propylene carbonate) (PPC) with H-T linkages over 83%, and number-average molecular weight (M-n) up to 100 kg/mol was synthesized at room temperature using Y(CCl3OO)(3)-ZnEt2-glycerine catalyst and 1,10-phenanthroline (PHEN) cocatalyst. Coordination of PHEN with active Zinc center enhanced the nucleophilic ability of the metal carbonate, which became more regio-specific in attacking carbon in PO, leading to PPC with improved H-T linkages. Moreover, the binding of PHEN to active Zinc center also raised the carbonate content of PPC to over 99%, whereas the PPC from common rare earth ternary catalyst was about 96%. Unlike the highly regio-regular structure PPC but with relatively low molecular weight recently reported in the literature, our high molecular weight regio-regular PPC did show significant improvement in thermal and mechanical performances. PPC with H-T linkages up to 83.2% showed glass transition temperature (T-g) of 43.3 degrees C, while T-g of PPC with H-T linkages of 69.7% was only 36.1 degrees C. When H-T connectivity was raised from 69.7 to 83.2%, the modulus of PPC showed a 78% increase. (c) 2008 Wiley Periodicals, Inc. |
| 语种 | 英语 |
| WOS记录号 | WOS:000257153500016 |
| 出版者 | JOHN WILEY & SONS INC |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/64253]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Wang, Xianhong |
| 作者单位 | 1.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
| 推荐引用方式 GB/T 7714 | Tao, Youhua,Wang, Xianhong,Chen, Xuesi,et al. Regio-regular structure high molecular weight poly(propylene carbonate) by rare earth ternary catalyst and Lewis base cocatalyst[J]. JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY,2008,46(13):4451-4458. |
| APA | Tao, Youhua,Wang, Xianhong,Chen, Xuesi,Zhao, Xiaojiang,&Wang, Fosong.(2008).Regio-regular structure high molecular weight poly(propylene carbonate) by rare earth ternary catalyst and Lewis base cocatalyst.JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY,46(13),4451-4458. |
| MLA | Tao, Youhua,et al."Regio-regular structure high molecular weight poly(propylene carbonate) by rare earth ternary catalyst and Lewis base cocatalyst".JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY 46.13(2008):4451-4458. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。