Tough Photonic Crystals Fabricated by Photo-Crosslinkage of Latex Spheres
文献类型：期刊论文
| 作者 | Tian, Entao2,3; Cui, Liying2,3; Wang, Jingxia1; Song, Yanlin1,2; Jiang, Lei2 |
| 刊名 | MACROMOLECULAR RAPID COMMUNICATIONS
 |
| 出版日期 | 2009-04-01 |
| 卷号 | 30期号:7页码:509-514 |
| 关键词 | Mechanical Strength Photo-crosslinkage Solvent Resistance Tough Photonic Crystals |
| ISSN号 | 1022-1336 |
| DOI | 10.1002/marc.200800731 |
| 英文摘要 | A general method to enhance the mechanical properties and solvent resistance of photonic crystals (PCs) has been demonstrated. This is carried out by the crosslinkage of latex spheres via photopolymerization of acrylamide (AAm) infiltrated among them. The crosslinked PAAm enhances the interaction among latex spheres of the PCs film, and contributes to the improvement of mechanical strength and solvent resistance. The result provides a simple approach to make tough PCs films by photo-crosslinkage, and can be extended to a wide variety of materials, will be of great importance for the practical application of PCs. |
| 语种 | 英语 |
| WOS记录号 | WOS:000265324300004 |
| 出版者 | WILEY-V C H VERLAG GMBH |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/66427]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Wang, Jingxia |
| 作者单位 | 1.Chinese Acad Sci, Inst Chem, New Mat Lab, Beijing 100190, Peoples R China 2.Chinese Acad Sci, Inst Chem, Key Lab Organ Solids, BNLMS, Beijing 100190, Peoples R China 3.Chinese Acad Sci, Grad Univ, Beijing 100190, Peoples R China |
| 推荐引用方式 GB/T 7714 | Tian, Entao,Cui, Liying,Wang, Jingxia,et al. Tough Photonic Crystals Fabricated by Photo-Crosslinkage of Latex Spheres[J]. MACROMOLECULAR RAPID COMMUNICATIONS,2009,30(7):509-514. |
| APA | Tian, Entao,Cui, Liying,Wang, Jingxia,Song, Yanlin,&Jiang, Lei.(2009).Tough Photonic Crystals Fabricated by Photo-Crosslinkage of Latex Spheres.MACROMOLECULAR RAPID COMMUNICATIONS,30(7),509-514. |
| MLA | Tian, Entao,et al."Tough Photonic Crystals Fabricated by Photo-Crosslinkage of Latex Spheres".MACROMOLECULAR RAPID COMMUNICATIONS 30.7(2009):509-514. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。