The formation of different structures of poly(3-hexylthiophene) film on a patterned substrate by dip coating from aged solution
文献类型：期刊论文
| 作者 | Xue, Longjian; Gao, Xiang; Zhao, Kui; Liu, Jiangang; Yu, Xinhong; Han, Yanchun |
| 刊名 | NANOTECHNOLOGY
 |
| 出版日期 | 2010-04-09 |
| 卷号 | 21期号:14 |
| ISSN号 | 0957-4484 |
| DOI | 10.1088/0957-4484/21/14/145303 |
| 英文摘要 | Different local morphologies of poly(3-hexylthiophene) (P3HT, M(w) = 87 000 and 30 000-40 000 g mol(-1)) are grown on a patterned substrate, which is composed of octadecyltrichlorosilane (OTS area) stripes on a silicon wafer (SiO(x) area), via dip coating from the aged solutions. Bundles of P3HT (M(w) = 87 000 g mol(-1)) nanorods on the SiOx area and long nanofibrillar crystals on the OTS area are generated simultaneously from the one-day-aged 1 mg ml(-1) solution, while oriented P3HT (M(w) = 30 000-40 000 g mol(-1)) nanofibrillar crystals parallel to the long axis of the OTS pattern form on the OTS area from the seven-days-aged solution (1 mg ml(-1)). Different dimensional sizes of the P3HT aggregate in the toluene solution upon aging and the flow of the solution from SiOx to the OTS area, on which the receding contact angle is larger than that on the SiOx area, determines the local structures of the P3HT film on the patterned substrate. |
| 语种 | 英语 |
| WOS记录号 | WOS:000275652200017 |
| 出版者 | IOP PUBLISHING LTD |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/69823]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Han, Yanchun |
| 作者单位 | Chinese Acad Sci, Changchun Inst Appl Chem, Grad Sch, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China |
| 推荐引用方式 GB/T 7714 | Xue, Longjian,Gao, Xiang,Zhao, Kui,et al. The formation of different structures of poly(3-hexylthiophene) film on a patterned substrate by dip coating from aged solution[J]. NANOTECHNOLOGY,2010,21(14). |
| APA | Xue, Longjian,Gao, Xiang,Zhao, Kui,Liu, Jiangang,Yu, Xinhong,&Han, Yanchun.(2010).The formation of different structures of poly(3-hexylthiophene) film on a patterned substrate by dip coating from aged solution.NANOTECHNOLOGY,21(14). |
| MLA | Xue, Longjian,et al."The formation of different structures of poly(3-hexylthiophene) film on a patterned substrate by dip coating from aged solution".NANOTECHNOLOGY 21.14(2010). |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。