Phosphine-free synthesis of Zn1-xCdxSe/ZnSe/ZnSexS1-x/ZnS core/multishell structures with bright and stable blue-green photoluminescence
文献类型：期刊论文
| 作者 | Shen, Huaibin1,2; Zhou, Changhua2; Xu, ShaSha2; Yu, Cailan3; Wang, Hongzhe2; Chen, Xia1; Li, Lin Song2 |
| 刊名 | JOURNAL OF MATERIALS CHEMISTRY
 |
| 出版日期 | 2011 |
| 卷号 | 21期号:16页码:6046-6053 |
| ISSN号 | 0959-9428 |
| DOI | 10.1039/c0jm03605f |
| 英文摘要 | Highly photoluminescent (PL) Zn1-xCdxSe/ZnSe/ZnSexS1-x/ZnS core/multishell nanocrystals were successfully synthesized by a phosphine-free method. Alloyed ZnSexS1-x was chosen as the shell material to epitaxially grow on pre-synthesized Zn1-xCdxSe nanocrystals. By decreasing the molar ratio between Se and S in ZnSexS1-x, the shell composition gradually changed from ZnSe to ZnS. The PL emissions of these core/multishell nanocrystals can be tuned from 450 to 530 nm. The PL quantum yields (QYs) of as-synthesized nanocrystals reached 50 to 75% with full width at half maximum (FWHM) between 28 and 45 nm. By an organic-aqueous phase transfer method, such core/multishell nanocrystals can be transferred into water successfully using an amphiphilic oligomer (polymaleic acid n-hexadecanol ester) as a surface coating agent. It was found that the shell thicknesses of the assynthesized core/multishell nanocrystals dramatically affected the phase transfer efficiency. Stability tests showed that the water-soluble Zn1-xCdxSe/ZnSe/ZnSexS1-x/ZnS core/multishell nanocrystals with 10 monolayers of shells had very high PL QY and stability in various physiological conditions. |
| 语种 | 英语 |
| WOS记录号 | WOS:000289260000033 |
| 出版者 | ROYAL SOC CHEMISTRY |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/71359]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Chen, Xia |
| 作者单位 | 1.Jilin Univ, Coll Life Sci, Changchun 130021, Peoples R China 2.Henan Univ, Minist Educ, Key Lab Special Funct Mat, Kaifeng 475004, Peoples R China 3.Chinese Acad Sci, Inst Chem, Key Lab Photochem, Beijing 100080, Peoples R China |
| 推荐引用方式 GB/T 7714 | Shen, Huaibin,Zhou, Changhua,Xu, ShaSha,et al. Phosphine-free synthesis of Zn1-xCdxSe/ZnSe/ZnSexS1-x/ZnS core/multishell structures with bright and stable blue-green photoluminescence[J]. JOURNAL OF MATERIALS CHEMISTRY,2011,21(16):6046-6053. |
| APA | Shen, Huaibin.,Zhou, Changhua.,Xu, ShaSha.,Yu, Cailan.,Wang, Hongzhe.,...&Li, Lin Song.(2011).Phosphine-free synthesis of Zn1-xCdxSe/ZnSe/ZnSexS1-x/ZnS core/multishell structures with bright and stable blue-green photoluminescence.JOURNAL OF MATERIALS CHEMISTRY,21(16),6046-6053. |
| MLA | Shen, Huaibin,et al."Phosphine-free synthesis of Zn1-xCdxSe/ZnSe/ZnSexS1-x/ZnS core/multishell structures with bright and stable blue-green photoluminescence".JOURNAL OF MATERIALS CHEMISTRY 21.16(2011):6046-6053. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。