PE/OMMT Nanocomposites Catalyzed by the OMMT-Intercalated Et[Ind](2)ZrCl2 in Slurry Polymerization: Effects of Organic Solvent on Ethylene Polymerization Behaviors and the Nanocomposite Structures
文献类型：期刊论文
| 作者 | Huang, Ying-Juan1,2; Qin, Ya-Wei1,2; Dong, Jin-Yong1 |
| 刊名 | JOURNAL OF APPLIED POLYMER SCIENCE
 |
| 出版日期 | 2011-01-05 |
| 卷号 | 119期号:1页码:190-200 |
| 关键词 | In Situ Intercalative Polymerization Slurry Polymerization Polyethylene (Pe) Ommt/et[Ind](2)Zrcl2 Nanocomposites |
| ISSN号 | 0021-8995 |
| DOI | 10.1002/app.32429 |
| 英文摘要 | In situ intercalative polymerization for ethylene monomers was carried out to produce PE-based hybrids through a slurry polymerization method. In this approach, organic solvent for olefin polymerization was found to be one of the most significant factors for the dispersion of the OMMT-intercalated Et[Ind](2)ZrCl2 catalysts, which determines that whether olefin monomers polymerize is in a well-defined confinement environment or not. Understanding the olefin polymerization occurring in between the nanoscale silicate layers of OMMT as well as the corresponding structure of OMMT in an organic polymerization solvent is a critical step toward tailoring and characterizing nanocomposites formed by OMMT in a polyolefin matrix. As we know, the Et[Ind](2)ZrCl2 catalyst and MAO are both better dissolved in toluene than that in hexane because of the larger polarity of toluene. Thus, in hexane the active sites of the OMMT/Et[Ind](2)ZrCl2 catalyst exist in the silicate layers of OMMT and the PE chains grow in the middle of them, while in toluene the active specimens are exposed in the gel formed by the OMMT-intercalated catalyst with MAO, which cause that the PE chains propagated in the mixture liquids. Consequently, when hexane is selected as the polymerization solvent, the formed PE-based nanocomposites have a good dispersion of OMMT and the nanofiller content (TGA measurement residue at 600 degrees C) is thus higher (>7.0 wt %). However, in toluene, most of the silicate layers of OMMT are agglomerated in the PE matrix. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 119: 190-200, 2011 |
| 语种 | 英语 |
| WOS记录号 | WOS:000284176000023 |
| 出版者 | WILEY-BLACKWELL |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/72113]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Dong, Jin-Yong |
| 作者单位 | 1.Chinese Acad Sci, Inst Chem, Joint Lab Polymer Sci & Mat, CAS Key Lab Engn Plast, Beijing 100190, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Huang, Ying-Juan,Qin, Ya-Wei,Dong, Jin-Yong. PE/OMMT Nanocomposites Catalyzed by the OMMT-Intercalated Et[Ind](2)ZrCl2 in Slurry Polymerization: Effects of Organic Solvent on Ethylene Polymerization Behaviors and the Nanocomposite Structures[J]. JOURNAL OF APPLIED POLYMER SCIENCE,2011,119(1):190-200. |
| APA | Huang, Ying-Juan,Qin, Ya-Wei,&Dong, Jin-Yong.(2011).PE/OMMT Nanocomposites Catalyzed by the OMMT-Intercalated Et[Ind](2)ZrCl2 in Slurry Polymerization: Effects of Organic Solvent on Ethylene Polymerization Behaviors and the Nanocomposite Structures.JOURNAL OF APPLIED POLYMER SCIENCE,119(1),190-200. |
| MLA | Huang, Ying-Juan,et al."PE/OMMT Nanocomposites Catalyzed by the OMMT-Intercalated Et[Ind](2)ZrCl2 in Slurry Polymerization: Effects of Organic Solvent on Ethylene Polymerization Behaviors and the Nanocomposite Structures".JOURNAL OF APPLIED POLYMER SCIENCE 119.1(2011):190-200. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。