Impact fracture morphology of copolyester toughened with a maleited core-shell impact modifier
文献类型：期刊论文
| 作者 | Yu, ZZ; Lei, M; Ou, YC; Yang, GS |
| 刊名 | ACTA POLYMERICA SINICA
 |
| 出版日期 | 2000-06-01 |
| 期号 | 3页码:275-279 |
| 关键词 | Toughness Morphology Blends Copolyester Impact Modifier |
| ISSN号 | 1000-3304 |
| 英文摘要 | A maleited impact modifier (TPEg) with polyethylene-octene rubber shell and semi-crystalline polymer core was used to toughen non-crystalline copolyester (PETG) resin. TPEg has a significant toughening effect on PETG. A sharp transition from brittle to super-tough states for PETG/TPEg blends occurred when the TPEg content was up to 10%. Although the maleited polyethylene-octene rubber (POEg) also results in a brittletough transition, this transition takes place at a higher POEg content indicating that the loss of thensile strength and modulus of PETG blends in more serious. The effects of TPEg on impact toughness of PETG blends are well reflected from their evolution processes of topography and morphology formed during the impact fracture testing. The impact fractured surface of PETG blend with 5 wt% TPEg exhibits a very small area of its slow crack growth region and feather-like markings in its fast crack growth region under low magnification, indicating a brittle appearance. Whereas the impact fractured surface of PETG blend with 10wt% TPEg exhibits a very large area of its slow crack growth region and some parabola-like markings in its fast crack growth region under low magnification. Moreover, an extensive shear yielding of matrix can be seen both in the slow and the fast crack growth regions of the PETG/TPEg(90/10) blend under high magnification. It may dissipate a significant amount of impact energy,thereby responsible for the super toughness. |
| 语种 | 英语 |
| WOS记录号 | WOS:000087933500005 |
| 出版者 | SCIENCE PRESS |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/76325]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Yu, ZZ |
| 作者单位 | Chinese Acad Sci, Inst Chem, Ctr Mol Sci, State Key Lab Engn Plast, Beijing 100080, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yu, ZZ,Lei, M,Ou, YC,et al. Impact fracture morphology of copolyester toughened with a maleited core-shell impact modifier[J]. ACTA POLYMERICA SINICA,2000(3):275-279. |
| APA | Yu, ZZ,Lei, M,Ou, YC,&Yang, GS.(2000).Impact fracture morphology of copolyester toughened with a maleited core-shell impact modifier.ACTA POLYMERICA SINICA(3),275-279. |
| MLA | Yu, ZZ,et al."Impact fracture morphology of copolyester toughened with a maleited core-shell impact modifier".ACTA POLYMERICA SINICA .3(2000):275-279. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。