Composite films of nanostructured polyaniline with poly(vinyl alcohol)
文献类型：期刊论文
| 作者 | Zhang, ZM; Wan, MX |
| 刊名 | SYNTHETIC METALS
 |
| 出版日期 | 2002-04-10 |
| 卷号 | 128期号:1页码:83-89 |
| 关键词 | Polyaniline Nanostructure Poly(Vinyl Alcohol) Composite Film Conductivity |
| ISSN号 | 0379-6779 |
| 英文摘要 | The uniform composite films of nanostructured polyaniline (PANI) (e.g. nanotubes or nanorods with 60-80 nm in diameter) were successfully fabricated by blending with water-soluble poly(vinyl alcohol) (PVA) as a matrix. The PANI nanostructures were synthesized by a template-free method in the presence of P-naphthalene sulfonic acid (beta-NSA) as a dopant. The molecular structures of PANI-beta-NSA and the related composite films were characterized by UV-Vis absorption spectrum, FTIR spectrum and X-ray diffraction. It was found that the electrical, thermal and mechanical properties of the composite films were affected by the content of nanostructured PANI-beta-NSA in the PVA matrix. The composite film with 16% PANI-beta-NSA showed the following physical properties: room-temperature conductivity is in the range 10(-2) S/cm, tensile strength similar to603 kg/cm(2), tensile modulus similar to4.36 x 10(5) kg/cm(2) and ultimate elongation similar to80%. (C) 2002 Elsevier Science B.V. All rights reserved. |
| 语种 | 英语 |
| WOS记录号 | WOS:000174922000013 |
| 出版者 | ELSEVIER SCIENCE SA |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/78083]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Wan, MX |
| 作者单位 | Chinese Acad Sci, Inst Chem, Ctr Mol Sci, Organ Solid Lab, Beijing 100080, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, ZM,Wan, MX. Composite films of nanostructured polyaniline with poly(vinyl alcohol)[J]. SYNTHETIC METALS,2002,128(1):83-89. |
| APA | Zhang, ZM,&Wan, MX.(2002).Composite films of nanostructured polyaniline with poly(vinyl alcohol).SYNTHETIC METALS,128(1),83-89. |
| MLA | Zhang, ZM,et al."Composite films of nanostructured polyaniline with poly(vinyl alcohol)".SYNTHETIC METALS 128.1(2002):83-89. |