On compatibilization and toughening of a copolyester with a maleated thermoplastic elastomer
文献类型：期刊论文
| 作者 | Yu, ZZ; Lei, M; Ou, YC; Yang, GS |
| 刊名 | POLYMER
 |
| 出版日期 | 2002-12-01 |
| 卷号 | 43期号:25页码:6993-7001 |
| 关键词 | Compatibilization Copolyester Polyethylene-octene Copolymer |
| ISSN号 | 0032-3861 |
| 英文摘要 | A maleated thermoplastic elastomer (TPEg) was prepared from maleic anhydride, grafting a mixture of polyethylene - octene elastomer and semi-crystalline polyolefin plastic (60/40 by weight) in a twin screw extruder. The non-grafted version (TPE) of the mixture was also prepared under the same processing conditions. The TPEg was employed to compatibilize and toughen amorphous copolyester PETG/TPE blends. The addition of the TPEg improves the compatibility between PETG and the TPE and results in fine dispersion of the TPE in the PETG matrix. At a fixed dispersed phase content of 15 wt%, a sharp brittle-ductile transition takes place, when the TPEg content in the dispersed phase increases from 20 to 30 wt%, namely, the TPEg content in the blends increases just from 3 to 4.5 wt%. After the brittle-ductile transition, the blends are maintained at super-tough level with notched impact strength more than twenty-fold higher than that of pure PETG plastic. The influence of the TPEg content on fractography of the PETG/TPE blends was also investigated. When the TPEg content in dispersed phase is below 20 wt%, the impact fracture surface shows a small area of slow crack growth region and numerous feather-like markings in fast crack growth region, indicating a brittle failure mode. While the TPEg content in the dispersed phase is above 30 wt%, the impact fracture surface exhibits drastically enlarged slow crack growth region and some parabolic markings in the fast crack growth region. Massive cavitation and extensive matrix shear yielding are predominant mechanisms of the impact energy dissipation upon impact testing. (C) 2002 Elsevier Science Ltd. All rights reserved. |
| 语种 | 英语 |
| WOS记录号 | WOS:000179075700039 |
| 出版者 | ELSEVIER SCI LTD |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/79059]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Yu, ZZ |
| 作者单位 | 1.Univ Sydney, Sch Aerosp Mech & Mechatron Engn, Ctr Adv Mat Technol, Sydney, NSW 2006, Australia 2.Chinese Acad Sci, Inst Chem, Ctr Mol Sci, State Key Lab Engn Plast, Beijing 100080, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yu, ZZ,Lei, M,Ou, YC,et al. On compatibilization and toughening of a copolyester with a maleated thermoplastic elastomer[J]. POLYMER,2002,43(25):6993-7001. |
| APA | Yu, ZZ,Lei, M,Ou, YC,&Yang, GS.(2002).On compatibilization and toughening of a copolyester with a maleated thermoplastic elastomer.POLYMER,43(25),6993-7001. |
| MLA | Yu, ZZ,et al."On compatibilization and toughening of a copolyester with a maleated thermoplastic elastomer".POLYMER 43.25(2002):6993-7001. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。