Preparation of La-Ti composite oxide nanocrystal and examination of their surface topography with atomic force microscope
文献类型：期刊论文
| 作者 | Gu, L; Wang, YL; Tang, LL; Zhu, JJ; Wu, JH |
| 刊名 | CHINESE CHEMICAL LETTERS
 |
| 出版日期 | 2003-04-01 |
| 卷号 | 14期号:4页码:429-432 |
| 关键词 | La-ti Composite Oxide Nanocrystal Surface Pattern Atomic Force Microscope |
| ISSN号 | 1001-8417 |
| 英文摘要 | With sol-gel method, nanometer La-Ti composite oxide was successfully prepared at a low temperature (750similar to800degreesC) using polyethylene glycol as dispersant. By means of atomic force microscope, the surface pattern, particle size distribution, and specific surface area were studied. The compound particle surface appears as a smooth sheet, the mean size of the compound is 25.38 nm. On the specific surface, the particle erects at a height of 4.69 nm. The surface area is 58.90 nm(2). The La-Ti composite oxide nanocrystal prefers to narrow and even particle size distribution and the homogeneity of surface topography. |
| 语种 | 英语 |
| WOS记录号 | WOS:000182738600031 |
| 出版者 | CHINESE CHEMICAL SOCIETY |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/79897]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Wang, YL |
| 作者单位 | 1.Chongqing Univ, Bioengn Coll, State Educ Minist, Natl Key Lab Biomech & Tissue Engn, Chongqing 400044, Peoples R China 2.Chinese Acad Sci, Inst Chem, Beijing 10083, Peoples R China |
| 推荐引用方式 GB/T 7714 | Gu, L,Wang, YL,Tang, LL,et al. Preparation of La-Ti composite oxide nanocrystal and examination of their surface topography with atomic force microscope[J]. CHINESE CHEMICAL LETTERS,2003,14(4):429-432. |
| APA | Gu, L,Wang, YL,Tang, LL,Zhu, JJ,&Wu, JH.(2003).Preparation of La-Ti composite oxide nanocrystal and examination of their surface topography with atomic force microscope.CHINESE CHEMICAL LETTERS,14(4),429-432. |
| MLA | Gu, L,et al."Preparation of La-Ti composite oxide nanocrystal and examination of their surface topography with atomic force microscope".CHINESE CHEMICAL LETTERS 14.4(2003):429-432. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。