Studies on the silicone resins cured with polymethylsilazanes at ambient temperature
文献类型：期刊论文
| 作者 | Zhang, YM; Huang, Y; Liu, XL; Yu, YZ |
| 刊名 | JOURNAL OF APPLIED POLYMER SCIENCE
 |
| 出版日期 | 2003-08-08 |
| 卷号 | 89期号:6页码:1702-1707 |
| 关键词 | Silicones Curing Of Polymers Thermal Properties Polymethylsilazanes Resins |
| ISSN号 | 0021-8995 |
| DOI | 10.1002/app.12433 |
| 英文摘要 | Polymethylsilazanes (PMS) were synthesized and used to cure silicone resins at ambient temperature. The curing degree of the silicone resins depends on the structure of PMS, and its concentration in the resin. Silicone resins of different structure and different silanol content can be cured to a satisfactory degree, if the concentration of the PMS is high enough. Silicone resins cured with PMS showed improved thermal stability in nitrogen, compared with that of the heat-cured counterparts. The mechanism of thermal decomposition of the silicone resins is discussed. The improvement of heat resistance using PMS as the curing agent is accounted for by diminished thermal rearrangement and degradation of the polysiloxane network initiated by silanol groups in the resins. (C) 2003 Wiley Periodicals, Inc. |
| 语种 | 英语 |
| WOS记录号 | WOS:000183355800036 |
| 出版者 | JOHN WILEY & SONS INC |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/80737]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Huang, Y |
| 作者单位 | Chinese Acad Sci, Inst Chem, Natl Key Lab Engn Plast, Beijing 100080, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, YM,Huang, Y,Liu, XL,et al. Studies on the silicone resins cured with polymethylsilazanes at ambient temperature[J]. JOURNAL OF APPLIED POLYMER SCIENCE,2003,89(6):1702-1707. |
| APA | Zhang, YM,Huang, Y,Liu, XL,&Yu, YZ.(2003).Studies on the silicone resins cured with polymethylsilazanes at ambient temperature.JOURNAL OF APPLIED POLYMER SCIENCE,89(6),1702-1707. |
| MLA | Zhang, YM,et al."Studies on the silicone resins cured with polymethylsilazanes at ambient temperature".JOURNAL OF APPLIED POLYMER SCIENCE 89.6(2003):1702-1707. |