Large-sized La2O3-TiO2 high refractive glasses with low SiO2 fraction by hot-press sintering
文献类型：期刊论文
| 作者 | Han, Jianjun1; Wang, Zhui1,2; Li, Jianqiang2; Li, Xiaoyu2; Li, Jiangtao3; He, Gang3; Xie, Jun1 |
| 刊名 | INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE
 |
| 出版日期 | 2019-07-01 |
| 卷号 | 10期号:3页码:371-377 |
| 关键词 | containerless solidification glass high refractive index hot-pressed sintering La2O3-TiO2 |
| ISSN号 | 2041-1286 |
| DOI | 10.1111/ijag.13154 |
| 英文摘要 | Owing to the ultrahigh refractive index, La2O3-TiO2 glass is regarded as a promising candidate material in the field of lens, gemstones, and many other optics. However, due to its extremely low glass-forming ability, it can only be obtained by rapid solidification processes such as melt quench or containerless solidification methods, leading to the limited size of as-solidified products (for example, 1-10 mm for containerless solidified sample), that are severely deferring the application of this novel high refractive glass. In this work, we aimed at preparing the larger sized bulk glasses over 10 mm, La2O3-TiO2 glasses were successfully prepared by hot-press sintering within the glass kinetic window. A small amount addition of SiO2 was found to effectively increase the glass-forming ability while keeping high refractive index. When the content of SiO2 was 15 mol%, its transmittance could reach 54% at 800 nm and 72% in the infrared region (1 mm thick). Meanwhile, its refractive index could keep ultrahigh value above 2.14. And the sintering mechanism was studied according to the sintering shrinkage curve. It indicates that the plastic flow was the main mass transfer way in the densification process. |
| WOS关键词 | CERAMICS ; NANOCERAMICS ; FABRICATION ; INDEX ; BULK |
| 资助项目 | National Natural Science Foundation of China[51432004] ; National Natural Science Foundation of China[51471158] ; National Natural Science Foundation of China[51674232] |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:000470786300010 |
| 出版者 | WILEY PERIODICALS, INC |
| 资助机构 | National Natural Science Foundation of China |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/29937]  |
| 专题 | 中国科学院过程工程研究所 |
| 通讯作者 | Li, Jianqiang |
| 作者单位 | 1.Chinese Acad Sci, Inst Proc Engn, CAS Key Lab Green Proc & Engn, Natl Engn Lab Hydrometallurg Cleaner Prod Technol, Beijing, Peoples R China 2.Wuhan Univ Technol, State Key Lab Silicate Mat Architectures, Wuhan, Hubei, Peoples R China 3.Chinese Acad Sci, Tech Inst Phys & Chem, Beijing, Peoples R China |
| 推荐引用方式 GB/T 7714 | Han, Jianjun,Wang, Zhui,Li, Jianqiang,et al. Large-sized La2O3-TiO2 high refractive glasses with low SiO2 fraction by hot-press sintering[J]. INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE,2019,10(3):371-377. |
| APA | Han, Jianjun.,Wang, Zhui.,Li, Jianqiang.,Li, Xiaoyu.,Li, Jiangtao.,...&Xie, Jun.(2019).Large-sized La2O3-TiO2 high refractive glasses with low SiO2 fraction by hot-press sintering.INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE,10(3),371-377. |
| MLA | Han, Jianjun,et al."Large-sized La2O3-TiO2 high refractive glasses with low SiO2 fraction by hot-press sintering".INTERNATIONAL JOURNAL OF APPLIED GLASS SCIENCE 10.3(2019):371-377. |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。