The tribological properties and wear mechanism of copper coated graphite doped Sialon ceramic composites at wide range temperature from 25 to 800 degrees C
文献类型：期刊论文
| 作者 | Sun, Qichun1,2; Wang, Zixi3; Yin, Bing1; Yang, Jun1; Liu, Jiongjie1,2; Liu, Yulin1,2; Cheng, Jun1; Zhu, Shengyu1; Qiao, Zhuhui1 |
| 刊名 | TRIBOLOGY INTERNATIONAL
 |
| 出版日期 | 2018-07-01 |
| 卷号 | 123页码:10-16 |
| 关键词 | Sialon matrix composite Tribological properties Wear mechanisms Wide range temperature |
| ISSN号 | 0301-679X |
| DOI | 10.1016/j.triboint.2018.03.002 |
| 通讯作者 | Yang, Jun(jyang@licp.cas.cn) ; Qiao, Zhuhui(zhqiao@licp.cas.cn) |
| 英文摘要 | High-performance Sialon composites with excellent tribological properties were successfully fabricated by doped copper coated graphite. Results showed that Sialons have an excellent wear resistance (wear rate at 10(-6) mm(3)/Nm) at 25 degrees C. When the temperature increases to 200-600 degrees C, the wear rate of beta-Sialon composites decreases about 5-10 times compared to S0. Especially for S2 (the content of copper coated graphite is 30 wt%) at 600 degrees C, the wear rate decreases by an order of magnitude and the friction coefficient is reduced to 0.5, which is 37.5% lower than SO. The self-lubrication mechanism of Sialons ascribed to the synergistic effect of graphite and copper at wide range temperature. |
| 收录类别 | SCI |
| WOS关键词 | DRY SLIDING WEAR ; MATRIX COMPOSITES ; AQUEOUS-SOLUTION ; DEGREES-C ; BEHAVIOR ; CUO ; ALLOY ; NANOPARTICLES ; FRICTION ; TESTS |
| WOS研究方向 | Engineering |
| WOS类目 | Engineering, Mechanical |
| 语种 | 英语 |
| WOS记录号 | WOS:000431161600002 |
| 出版者 | ELSEVIER SCI LTD |
| URI标识 | http://www.irgrid.ac.cn/handle/1471x/2557852 |
| 专题 | 寒区旱区环境与工程研究所 |
| 通讯作者 | Yang, Jun; Qiao, Zhuhui |
| 作者单位 | 1.Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou, Gansu, Peoples R China 2.Univ Chinese Acad Sci, Beijing, Peoples R China 3.Tsinghua Univ, Dept Mech Engn, State Key Lab Tribol, Beijing, Peoples R China |
| 推荐引用方式 GB/T 7714 | Sun, Qichun,Wang, Zixi,Yin, Bing,et al. The tribological properties and wear mechanism of copper coated graphite doped Sialon ceramic composites at wide range temperature from 25 to 800 degrees C[J]. TRIBOLOGY INTERNATIONAL,2018,123:10-16. |
| APA | Sun, Qichun.,Wang, Zixi.,Yin, Bing.,Yang, Jun.,Liu, Jiongjie.,...&Qiao, Zhuhui.(2018).The tribological properties and wear mechanism of copper coated graphite doped Sialon ceramic composites at wide range temperature from 25 to 800 degrees C.TRIBOLOGY INTERNATIONAL,123,10-16. |
| MLA | Sun, Qichun,et al."The tribological properties and wear mechanism of copper coated graphite doped Sialon ceramic composites at wide range temperature from 25 to 800 degrees C".TRIBOLOGY INTERNATIONAL 123(2018):10-16. |
入库方式： iSwitch采集
来源：寒区旱区环境与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。