Dislocation loops in ultra-high purity Fe(Cr) alloys after 7.2 MeV proton irradiation
文献类型:期刊论文
作者 | Chen, J.1; Duval, F.2; Jung, P.1; Schaublin, R.3; Gao, N.4; Barthe, M. F.2 |
刊名 | JOURNAL OF NUCLEAR MATERIALS |
出版日期 | 2018-05-01 |
卷号 | 503页码:81-90 |
ISSN号 | 0022-3115 |
关键词 | Irradiation High purity Fe(Cr) alloys TEM observation Dislocation |
DOI | 10.1016/j.jnucmat.2018.02.042 |
通讯作者 | Chen, J.(jiachao.chen@psi.ch) |
英文摘要 | Ultra-high purity Fe(Cr) alloys (from 0 wt% Cr to 14 wt% Cr) were 3D homogeneously irradiated by 0-7.2 MeV protons to 0.3 dpa at nominal temperatures from 270 degrees C to 500 degrees C. Microstructural changes were observed by transmission electron microscopy (TEM). The results showed that evolution of dislocation loops depends on the Cr content. Below 300 degrees C, large 1/2 a(0) < 111 > loops are dominating. Above 300 degrees C, a(0) < 100 > loops with a habit plane {100} appear. Loop sizes of both types are more or less the same. At temperatures from 310 degrees C to 400 degrees C, a(0) < 100 > loops form clusters with the same {100} habit plane as the one of the loops forming them. This indicates that < 100 > loops of the same variant start gliding under mutual elastic interaction. At 500 degrees C, dislocation loops form disc shaped clusters about 1000 nm in diameter and sitting on {111} and/or {100} planes in the pure Fe samples. Based on these observations a quantitative analysis of the dislocation loops configurations and their temperature dependence is made, leading to an understanding of the basic mechanisms of formation of these loops. (C) 2018 Elsevier B.V. All rights reserved. |
收录类别 | SCI |
WOS关键词 | FE-CR ALLOYS ; HEAVY-ION IRRADIATIONS ; NEUTRON-IRRADIATION ; ALPHA-IRON ; PURE IRON ; INTERSTITIAL CLUSTERS ; TEM CHARACTERIZATION ; DAMAGE EVOLUTION ; FERRITIC STEEL ; THIN-FOILS |
WOS研究方向 | Materials Science ; Nuclear Science & Technology |
WOS类目 | Materials Science, Multidisciplinary ; Nuclear Science & Technology |
语种 | 英语 |
出版者 | ELSEVIER SCIENCE BV |
WOS记录号 | WOS:000429498200009 |
URI标识 | http://www.irgrid.ac.cn/handle/1471x/2558138 |
专题 | 寒区旱区环境与工程研究所 |
通讯作者 | Chen, J. |
作者单位 | 1.Paul Scherrer Inst, Dept Nucl Energy & Safety, CH-5232 Villigen, Switzerland 2.Univ Orleans, CNRS, CEMHTI, 3A Rue Ferollerie, F-45071 Orleans 2, France 3.ETH, Sci Ctr Opt & Electron Microscopy, CH-8093 Zurich, Switzerland 4.Chinese Acad Sci, Inst Modern Phys, Lanzhou, Gansu, Peoples R China |
推荐引用方式 GB/T 7714 | Chen, J.,Duval, F.,Jung, P.,et al. Dislocation loops in ultra-high purity Fe(Cr) alloys after 7.2 MeV proton irradiation[J]. JOURNAL OF NUCLEAR MATERIALS,2018,503:81-90. |
APA | Chen, J.,Duval, F.,Jung, P.,Schaublin, R.,Gao, N.,&Barthe, M. F..(2018).Dislocation loops in ultra-high purity Fe(Cr) alloys after 7.2 MeV proton irradiation.JOURNAL OF NUCLEAR MATERIALS,503,81-90. |
MLA | Chen, J.,et al."Dislocation loops in ultra-high purity Fe(Cr) alloys after 7.2 MeV proton irradiation".JOURNAL OF NUCLEAR MATERIALS 503(2018):81-90. |
入库方式: iSwitch采集
来源:寒区旱区环境与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。