Radial X-ray diffraction study of the static strength and texture of tungsten to 96 GPa
文献类型：期刊论文
| 作者 | Liu, J ; Bai LG(白利刚); Li XD(李晓东); Liu J(刘景); Tang, YM; Li, B; Xiong, L; Li, Q; Hao, JB; Bai, LG
|
| 刊名 | SOLID STATE COMMUNICATIONS
 |
| 出版日期 | 2018 |
| 卷号 | 269页码:83-89 |
| 关键词 | W High pressure Strength Texture Radial X-ray diffraction DAC |
| ISSN号 | 0038-1098 |
| DOI | 10.1016/j.ssc.2017.10.016 |
| 文献子类 | Article |
| 英文摘要 | Investigations of equation of state, strength and texture of tungsten (W) have been performed under non hydrostatic compression up to 96 GPa using an angle-dispersive radial X-ray diffraction (RXRD) techniques together with the lattice strain theory in a 2-fold paranomic diamond anvil cell (DAC) at ambient temperature. The ratio of t/G is found to remain constant above similar to 35 GPa, indicating that the W started to experience macro yield with plastic deformation at this pressure. Combined with independent constraints on the high-pressure shear modulus, we found that W sample could support a differential stress of similar to 4.57 GPa when it started to yield with plastic deformation at similar to 35 GPa under uniaxial compression. The differential stress in W ranges from 0.01 GPa to 1.46 GPa with pressure increasing from 6 GPa to 35 GPa and can be described as t = -0.904(136) + 0.154(6)P, where P is the pressure in GPa. A maximum differential stress, as high as similar to 6.46 GPa can be supported by W at the highest pressure of similar to 96 GPa. In addition, we have investigated the texture of W under nonhydrostatic compression up to the highest pressure of 96 GPa using the software package MAUD (Material Analysis Using Diffraction). It is convinced that the plastic deformation due to stress under high pressures is responsible for the development of texture. |
| 电子版国际标准刊号 | 1879-2766 |
| WOS关键词 | SHEAR-STRENGTH ; HIGH-PRESSURE ; LATTICE STRAINS ; COMPRESSION ; CALIBRATION ; MOLYBDENUM ; METALS ; GAUGE ; IRON ; MBAR |
| WOS研究方向 | Physics |
| 语种 | 英语 |
| WOS记录号 | WOS:000418276700016 |
| 源URL | [http://ir.ihep.ac.cn/handle/311005/285507]  |
| 专题 | 高能物理研究所_多学科研究中心 |
| 作者单位 | 中国科学院高能物理研究所 |
| 推荐引用方式 GB/T 7714 | Liu, J,Bai LG,Li XD,et al. Radial X-ray diffraction study of the static strength and texture of tungsten to 96 GPa[J]. SOLID STATE COMMUNICATIONS,2018,269:83-89. |
| APA | Liu, J.,白利刚.,李晓东.,刘景.,Tang, YM.,...&Li, XD.(2018).Radial X-ray diffraction study of the static strength and texture of tungsten to 96 GPa.SOLID STATE COMMUNICATIONS,269,83-89. |
| MLA | Liu, J,et al."Radial X-ray diffraction study of the static strength and texture of tungsten to 96 GPa".SOLID STATE COMMUNICATIONS 269(2018):83-89. |
入库方式： OAI收割
来源：高能物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。