Static strength of molybdenum to 92 GPa under radial X-ray diffraction
文献类型：期刊论文
| 作者 | Bai, LG; Xiong L(熊伦) ; Xiong, L; Tu, P; Li, B; Wu, SY; Hao, JB; Li, XD; Liu, J; Bai LG(白利刚)
|
| 刊名 | INTERNATIONAL JOURNAL OF MODERN PHYSICS B
 |
| 出版日期 | 2018 |
| 卷号 | 32期号:14页码:1850177 |
| 关键词 | Molybdenum strength radial X-ray diffraction high pressure |
| ISSN号 | 0217-9792 |
| DOI | 10.1142/S0217979218501771 |
| 文献子类 | Article |
| 英文摘要 | The high-pressure strength of molybdenum (Mo) to 92 GPa has been studied by radial X-ray diffraction (RXRD) technique. The ratio of t/G is found to decrease above similar to 24 GPa, showing the yield of Mo which is caused by plastic deformation at this pressure. Combined with high-pressure shear modulus, it was found that the differential stress corresponding to the yield of Mo at 24 GPa due to plastic deformation is 1.73 GPa. The second increase of t values occurs after similar to 66 GPa, suggesting the strength of Mo with a differential stress of similar to 1.93 GPa. In addition, the maximum difference stress of molybdenum at 87 GPa is 3.01 GPa. |
| 电子版国际标准刊号 | 1793-6578 |
| WOS关键词 | EQUATION-OF-STATE ; ELASTIC-CONSTANTS ; NONHYDROSTATIC COMPRESSION ; LATTICE STRAINS ; PRESSURE ; MO ; TUNGSTEN ; RHENIUM ; ALLOYS ; METALS |
| WOS研究方向 | Physics |
| 语种 | 英语 |
| WOS记录号 | WOS:000434346700013 |
| 源URL | [http://ir.ihep.ac.cn/handle/311005/286038]  |
| 专题 | 高能物理研究所_多学科研究中心 |
| 通讯作者 | Xiong L(熊伦) |
| 作者单位 | 中国科学院高能物理研究所 |
| 推荐引用方式 GB/T 7714 | Bai, LG,Xiong L,Xiong, L,et al. Static strength of molybdenum to 92 GPa under radial X-ray diffraction[J]. INTERNATIONAL JOURNAL OF MODERN PHYSICS B,2018,32(14):1850177. |
| APA | Bai, LG.,熊伦.,Xiong, L.,Tu, P.,Li, B.,...&刘景.(2018).Static strength of molybdenum to 92 GPa under radial X-ray diffraction.INTERNATIONAL JOURNAL OF MODERN PHYSICS B,32(14),1850177. |
| MLA | Bai, LG,et al."Static strength of molybdenum to 92 GPa under radial X-ray diffraction".INTERNATIONAL JOURNAL OF MODERN PHYSICS B 32.14(2018):1850177. |
入库方式： OAI收割
来源：高能物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。