Effect of Re content on precipitation behaviour of secondary phases in a single-crystal Ni-based superalloy during high-temperature thermal exposure
文献类型：期刊论文
| 作者 | Liu, LR; Chen, MK; Tian, SG; Zhang, ZY; Jin, T |
| 刊名 | MATERIALS AT HIGH TEMPERATURES
 |
| 出版日期 | 2018-02-06 |
| 卷号 | 35期号:4页码:355-362 |
| 关键词 | Single-crystal superalloy rhenium precipitated phase thermal exposure |
| ISSN号 | 0960-3409 |
| DOI | 10.1080/09603409.2017.1367155 |
| 英文摘要 | The precipitation of secondary phases in single-crystal Ni-based superalloys with different contents of Re are investigated using TEM and SEM.The results show that after full heat treatment, the size of secondary gamma' phase decreases gradually with increasing Re content. During long-term thermal exposure at 1093 degrees C, some needle-like and rod-like secondary phases precipitate from the gamma matrix. With increasing Re content and prolonging of the thermal exposure, the amounts of precipitated phases clearly increase. In the alloy with 2.5 wt-% Re, the needle-like phases are identified as M6C carbides. In the alloy with 3 wt-% Re, both M6C carbides and mu phase are found. In the alloy with 15 wt% Re, the needle-like and rod-like precipitated phases are identified as mu and P phases. Stacking fault was found in the P phase and that part was identified as mu phase by SAD; that is, there is intergrowth of P and mu phases. |
| 学科主题 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000432282500006 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/80255]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.Shenyang Univ Technol, Mat Sci & Engn Sch, Shenyang, Liaoning, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Dept Superalloys, Shenyang, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu, LR,Chen, MK,Tian, SG,et al. Effect of Re content on precipitation behaviour of secondary phases in a single-crystal Ni-based superalloy during high-temperature thermal exposure[J]. MATERIALS AT HIGH TEMPERATURES,2018,35(4):355-362. |
| APA | Liu, LR,Chen, MK,Tian, SG,Zhang, ZY,&Jin, T.(2018).Effect of Re content on precipitation behaviour of secondary phases in a single-crystal Ni-based superalloy during high-temperature thermal exposure.MATERIALS AT HIGH TEMPERATURES,35(4),355-362. |
| MLA | Liu, LR,et al."Effect of Re content on precipitation behaviour of secondary phases in a single-crystal Ni-based superalloy during high-temperature thermal exposure".MATERIALS AT HIGH TEMPERATURES 35.4(2018):355-362. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。