Improvement of Strength-Toughness-Hardness Balance in Large Cross-Section 718H Pre-Hardened Mold Steel
文献类型：期刊论文
| 作者 | Liu, HH; Fu, PX; Liu, HW; Li, DZ |
| 刊名 | MATERIALS
 |
| 出版日期 | 2018-04-01 |
| 卷号 | 11期号:4页码:- |
| 关键词 | 718H pre-hardened mold steel heat treatments strength-toughness-hardness microstructure |
| ISSN号 | 1996-1944 |
| DOI | 10.3390/ma11040583 |
| 英文摘要 | The strength-toughness combination and hardness uniformity in large cross-section 718H pre-hardened mold steel from a 20 ton ingot were investigated with three different heat treatments for industrial applications. The different microstructures, including tempered martensite, lower bainite, and retained austenite, were obtained at equivalent hardness. The microstructures were characterized by using metallographic observations, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and electron back-scattered diffraction (EBSD). The mechanical properties were compared by tensile, Charpy U-notch impact and hardness uniformity tests at room temperature. The results showed that the test steels after normalizing-quenching-tempering (N-QT) possessed the best strength-toughness combination and hardness uniformity compared with the conventional quenched-tempered (QT) steel. In addition, the test steel after austempering-tempering (A-T) demonstrated the worse hardness uniformity and lower yield strength while possessing relatively higher elongation (17%) compared with the samples after N-QT (14.5%) treatments. The better ductility of A-T steel mainly depended on the amount and morphology of retained austenite and thermal/deformation-induced twined martensite. This work elucidates the mechanisms of microstructure evolution during heat treatments and will highly improve the strength-toughness-hardness trade-off in large cross-section steels. |
| 学科主题 | Materials Science, Multidisciplinary |
| 语种 | 英语 |
| WOS记录号 | WOS:000434710200125 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/80216]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, 72 Wenhua Rd, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, 72 Wenhua Rd, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu, HH,Fu, PX,Liu, HW,et al. Improvement of Strength-Toughness-Hardness Balance in Large Cross-Section 718H Pre-Hardened Mold Steel[J]. MATERIALS,2018,11(4):-. |
| APA | Liu, HH,Fu, PX,Liu, HW,&Li, DZ.(2018).Improvement of Strength-Toughness-Hardness Balance in Large Cross-Section 718H Pre-Hardened Mold Steel.MATERIALS,11(4),-. |
| MLA | Liu, HH,et al."Improvement of Strength-Toughness-Hardness Balance in Large Cross-Section 718H Pre-Hardened Mold Steel".MATERIALS 11.4(2018):-. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。