Effect of Pseudomonas sp on the degradation of aluminum/epoxy coating in seawater
文献类型：期刊论文
| 作者 | Feng, TT; Wu, JY; Chai, K; Liu, FC |
| 刊名 | JOURNAL OF MOLECULAR LIQUIDS
 |
| 出版日期 | 2018-08-01 |
| 卷号 | 263页码:248-254 |
| 关键词 | Pseudomonas sp. Degradation Aluminum/epoxy coating Seawater |
| ISSN号 | 0167-7322 |
| DOI | 10.1016/j.molliq.2018.04.103 |
| 英文摘要 | Polymeric coatings prevent metal materials from corrosion. Nevertheless, the degradation of the coatings in sea-water by microorganisms is almost unknown. In this work, we explored the degradation of the aluminum/epoxy coating in sterile seawater and seawater inoculated with Pseudomonas sp. by electrochemical impedance spectroscopy, scanning electron microscopy, energy dispersive spectroscopy, Fourier transform infrared spectroscopy and contact angle test. The decreases in the corrosion resistance of the coating were significantly higher in seawater inoculated with Pseudomonas sp. than in sterile seawater. The mature biofilm formed on the coating and then the extensive under-coating corrosion occurred in seawater inoculated with Pseudomonas sp.. These results revealed that Pseudomonas sp. significantly decreased the corrosion resistance of the coating and might degrade the coating. Some bulges and tiny holes were observed on the coating in seawater inoculated with Pseudomonas sp.. The contents of Al and O significantly respectively decreased and increased on the surface of the coating in seawater inoculated with Pseudomonas sp. relative to those on the surfaces of the coating without immersion and in sterile seawater. The absorbance of the C-OH peak for the coating immersed in seawater inoculated with Pseudomonas sp. was significantly higher than that for the coating without immersion and the coating immersed in sterile seawater. Moreover, Pseudomonas sp. decreased the water contact angle of the coating surfaces. The results demonstrated that Pseudomonas sp. degraded the aluminum/epoxy coating through decomposing the aluminum and oxidizing the epoxy to forming hydroxyl. (C) 2018 Elsevier B.V. All rights reserved. |
| 学科主题 | Chemistry, Physical ; Physics, Atomic, Molecular & Chemical |
| 语种 | 英语 |
| WOS记录号 | WOS:000436911300029 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/80078]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.Hainan Univ, Mat & Chem Engn Coll, Minist Educ, Key Lab Adv Mat Trop Isl Resources, Haikou 570228, Hainan, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Feng, TT,Wu, JY,Chai, K,et al. Effect of Pseudomonas sp on the degradation of aluminum/epoxy coating in seawater[J]. JOURNAL OF MOLECULAR LIQUIDS,2018,263:248-254. |
| APA | Feng, TT,Wu, JY,Chai, K,&Liu, FC.(2018).Effect of Pseudomonas sp on the degradation of aluminum/epoxy coating in seawater.JOURNAL OF MOLECULAR LIQUIDS,263,248-254. |
| MLA | Feng, TT,et al."Effect of Pseudomonas sp on the degradation of aluminum/epoxy coating in seawater".JOURNAL OF MOLECULAR LIQUIDS 263(2018):248-254. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。