High efficiency dispersal and strengthening of graphene reinforced aluminum alloy composites fabricated by powder metallurgy combined with friction stir processing
文献类型：期刊论文
| 作者 | Zhang, ZW; Liu, ZY; Xiao, BL; Ni, DR; Ma, ZY |
| 刊名 | CARBON
 |
| 出版日期 | 2018-08-01 |
| 卷号 | 135页码:215-223 |
| ISSN号 | 0008-6223 |
| DOI | 10.1016/j.carbon.2018.04.029 |
| 英文摘要 | 1 wt.% graphene nanoplatelets reinforced 2009Al (GNP/2009Al) composites were fabricated by a combination of powder metallurgy and subsequent multi-pass friction stir processing (FSP). Microstructural examinations showed that the GNP distribution was significantly improved as the number of FSP passes increased, with a uniform dispersion of GNPs achieved after 2 FSP passes. The layered structures of GNPs were well retained and most of the GNP-Al interfaces were clean and well bonded in FSP composites. Tensile tests showed that the strengths and the elongation of the composites increased initially and then decreased, as the number of FSP passes increased from 1 to 4 passes. In particular, the 2-pass FSP composite exhibited a maximum ultimate tensile strength and yield strength of 514 MPa and 398MPa, an increase of 23.3% and 30.5%, respectively, compared with 2009Al alloy. Moreover, a sound elongation of 10% was obtained for the 2-pass FSP composite. A strength calculation based on load transfer indicated that the high efficiency strengthening of the composite could be attributed to the large specific surface area of uniformly dispersed GNPs. (C) 2018 Elsevier Ltd. All rights reserved. |
| 学科主题 | Chemistry, Physical ; Materials Science, Multidisciplinary |
| 语种 | 英语 |
| WOS记录号 | WOS:000436800100024 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/80077]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.[Zhang, Z. W. 2.Liu, Z. Y. 3.Xiao, B. L. 4.Ni, D. R. 5.Ma, Z. Y.] Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, ZW,Liu, ZY,Xiao, BL,et al. High efficiency dispersal and strengthening of graphene reinforced aluminum alloy composites fabricated by powder metallurgy combined with friction stir processing[J]. CARBON,2018,135:215-223. |
| APA | Zhang, ZW,Liu, ZY,Xiao, BL,Ni, DR,&Ma, ZY.(2018).High efficiency dispersal and strengthening of graphene reinforced aluminum alloy composites fabricated by powder metallurgy combined with friction stir processing.CARBON,135,215-223. |
| MLA | Zhang, ZW,et al."High efficiency dispersal and strengthening of graphene reinforced aluminum alloy composites fabricated by powder metallurgy combined with friction stir processing".CARBON 135(2018):215-223. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。