Effect of corrosion product films on the in vitro degradation behavior of Mg-3%Al-1%Zn (in wt%) alloy in Hank's solution
文献类型：期刊论文
| 作者 | Wang, BJ; Xu, DK; Dong, JH; Ke, W |
| 刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2018-10-01 |
| 卷号 | 34期号:10页码:1756-1764 |
| 关键词 | Magnesium Surface layer Corrosion product Interface |
| ISSN号 | 1005-0302 |
| DOI | 10.1016/j.jmst.2018.02.013 |
| 英文摘要 | Through investigating the corrosion behavior of an as-extruded Mg-3wt%Al-1 wt%Zn (AZ31) alloy in a simulated physiological fluid of Hank's solution, it demonstrates that the corrosion process was dependent on the immersion time. Further analyses revealed that the highest corrosion resistance could be obtained at 24 h due to the formation of a compact layer of corrosion products on the sample surface. With increasing the immersion time to up to 48 h, the thickness of surface films increased gradually but obvious de-bonding of such film from the substrate could take place, resulting in a certain resilience of the overall corrosion resistance. (C) 2018 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| 学科主题 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000438131700006 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/79943]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.[Wang, B. J.] Shenyang Ligong Univ, Sch Environm & Chem Engn, Shenyang 110159, Liaoning, Peoples R China 2.[Xu, D. K. 3.Ke, W.] Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China 4.[Xu, D. K. 5.Dong, J. H. 6.Ke, W.] Chinese Acad Sci, Inst Met Res, Environm Corros Ctr, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang, BJ,Xu, DK,Dong, JH,et al. Effect of corrosion product films on the in vitro degradation behavior of Mg-3%Al-1%Zn (in wt%) alloy in Hank's solution[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2018,34(10):1756-1764. |
| APA | Wang, BJ,Xu, DK,Dong, JH,&Ke, W.(2018).Effect of corrosion product films on the in vitro degradation behavior of Mg-3%Al-1%Zn (in wt%) alloy in Hank's solution.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,34(10),1756-1764. |
| MLA | Wang, BJ,et al."Effect of corrosion product films on the in vitro degradation behavior of Mg-3%Al-1%Zn (in wt%) alloy in Hank's solution".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 34.10(2018):1756-1764. |