Interfacial Microstructural Evolution and Metallurgical Bonding Mechanisms for IN718 Superalloy Joint Produced by Hot Compressive Bonding
文献类型：期刊论文
| 作者 | Zhang, JY; Sun, MY; Xu, B1; Li, DZ |
| 刊名 | METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE
 |
| 出版日期 | 2018-10-01 |
| 卷号 | 49期号:5页码:2152-2162 |
| ISSN号 | 1073-5615 |
| DOI | 10.1007/s11663-018-1313-9 |
| 英文摘要 | The novel metallurgical joining process for bonding IN718 superalloy was investigated by hot compressive bonding (HCB) process under the deformation temperature range of 1000 A degrees C to 1150 A degrees C and true strains ranging from 0 to 0.5 at a strain rate of 0.001 s(-1). The effect of HCB process parameters on the tensile strength was analyzed. Both the as-deformed and the interfacial microstructures were characterized using the optical microscope, electron backscattered diffraction and transmission electron microscope (TEM) analysis. The results of tensile property revealed that the degree of metallurgical bonding is promoted by increasing deformation temperature and strain. The evolution of the interfacial microstructure showed that the migration of interfacial grain boundary (IGB), which is characterized by discontinuous dynamic recrystallization, is the dominant metallurgical bonding mechanism in the early stages of bonding. TEM analysis indicated that the dislocation density is distributed heterogeneously over both sides of IGB, which is the significant reason for the migration of IGB, during the initial stage of HCB process. |
| 学科主题 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000444765500003 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/79928]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, JY,Sun, MY,Xu, B,et al. Interfacial Microstructural Evolution and Metallurgical Bonding Mechanisms for IN718 Superalloy Joint Produced by Hot Compressive Bonding[J]. METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE,2018,49(5):2152-2162. |
| APA | Zhang, JY,Sun, MY,Xu, B,&Li, DZ.(2018).Interfacial Microstructural Evolution and Metallurgical Bonding Mechanisms for IN718 Superalloy Joint Produced by Hot Compressive Bonding.METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE,49(5),2152-2162. |
| MLA | Zhang, JY,et al."Interfacial Microstructural Evolution and Metallurgical Bonding Mechanisms for IN718 Superalloy Joint Produced by Hot Compressive Bonding".METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE 49.5(2018):2152-2162. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。