Notch fracture toughness of body-centered-cubic (TiZrNbTa)-Mo high-entropy alloys
文献类型：期刊论文
| 作者 | Wang, SP; Ma, E2; Xu, J |
| 刊名 | INTERMETALLICS
 |
| 出版日期 | 2018-12-01 |
| 卷号 | 103页码:78-87 |
| ISSN号 | 0966-9795 |
| 关键词 | High-entropy alloys Fracture toughness BCC structure Nanoindentation Dislocation |
| DOI | 10.1016/J.intermet.2018.10.008 |
| 英文摘要 | The notch fracture toughness (K-Q) and its dependence on Mo concentration in as-cast body-centered-cubic (TiZrNbTa)(100-x)Mo-x high-entropy alloys have been measured at room temperature. It is shown that the increase of Mo concentration results in a significant reduction in fracture toughness, with the K-Q decreasing from 28.5 MPa root m for the Mo-free TiZrNbTa quaternary alloy to 18.7 MPaVin for the TiZrNbTaMo quinary alloy. The K-Q of these HEAs scales inversely with increasing (d + s) electrons per atom. The fracture mode under Mode I loading transists from monolithic intergranular fracture for Mo-free TiZrNbTa to completely transgranular cleavage for the TiZrNbTaMo alloy. The brittleness is consistent with the known effects of refractory solutes on increasing the brittle-to-ductile transition temperature in Nb-based solutions. The embrittlement effect with alloying (especially Mo) is also attributable to the elevation of the critical temperature (T-0), making the activation to overcome lattice resistance to dislocation motion increasingly difficult. The low ratio T/T-0 (T = 300 K in our case) can in fact be inferred from the very small activation volume (3b(3)) measured for TiZrNbTa and TiZrNbTaMo. |
| 学科主题 | Chemistry, Physical ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000450380700010 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/79789]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China 2.Univ Chinese Acad Sci, 19 A Yuquan Rd, Beijing 100049, Peoples R China 3.Johns Hopkins Univ, Dept Mat Sci & Engn, Baltimore, MD 21218 USA |
| 推荐引用方式 GB/T 7714 | Wang, SP,Ma, E,Xu, J. Notch fracture toughness of body-centered-cubic (TiZrNbTa)-Mo high-entropy alloys[J]. INTERMETALLICS,2018,103:78-87. |
| APA | Wang, SP,Ma, E,&Xu, J.(2018).Notch fracture toughness of body-centered-cubic (TiZrNbTa)-Mo high-entropy alloys.INTERMETALLICS,103,78-87. |
| MLA | Wang, SP,et al."Notch fracture toughness of body-centered-cubic (TiZrNbTa)-Mo high-entropy alloys".INTERMETALLICS 103(2018):78-87. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。