The effect of surface modification of zinc particles with phosphoric acid on the corrosion resistance of cold galvanizing coatings
文献类型：期刊论文
| 作者 | Xu, L; Liu, FC; Wang, ZY; Ke, W; Han, EH; Jie, GX; Wang, J; Huang, HJ; Liu, FC (reprint author), Chinese Acad Sci, Key Lab Nucl Mat & Safety Assessment, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China. |
| 刊名 | PROGRESS IN ORGANIC COATINGS
 |
| 出版日期 | 2018 |
| 卷号 | 114页码:90-101 |
| 关键词 | Rich Powder Coatings Electrochemical Impedance Spectroscopy Artificial Sea-water Nacl Solution Coated Steel Paints Phosphate Behavior Eis Improvement |
| ISSN号 | 0300-9440 |
| 英文摘要 | The surface modification of zinc particles using phosphoric acid was conducted to improve the corrosion resistance of Cold galvanizing coatings. The modified zinc particles were characterized by Scanning Electron Microscope (SEM) and X-ray diffraction (XRD). Electrochemical impedance spectroscopy (EIS) and Scanning Vibrating Electrode Technique (SVET) were performed to investigate the corrosion protection mechanism of the coating. The electrochemical activity of zinc particles were found decreased because of the formation of Zn-3(PO4)center dot 4H(2)O on the surface of the particle. Little lamellar-shaped phosphate was also observed after surface modification. The best anti-corrosion performance of the coating was achieved when using zinc particles modified with 1% phosphoric acid as the fillings. This improvement was accomplished by the combined effect of reduced electrochemical activity of surface modified zinc particles and block effect from lamellar-shaped phosphate.; The surface modification of zinc particles using phosphoric acid was conducted to improve the corrosion resistance of Cold galvanizing coatings. The modified zinc particles were characterized by Scanning Electron Microscope (SEM) and X-ray diffraction (XRD). Electrochemical impedance spectroscopy (EIS) and Scanning Vibrating Electrode Technique (SVET) were performed to investigate the corrosion protection mechanism of the coating. The electrochemical activity of zinc particles were found decreased because of the formation of Zn-3(PO4)center dot 4H(2)O on the surface of the particle. Little lamellar-shaped phosphate was also observed after surface modification. The best anti-corrosion performance of the coating was achieved when using zinc particles modified with 1% phosphoric acid as the fillings. This improvement was accomplished by the combined effect of reduced electrochemical activity of surface modified zinc particles and block effect from lamellar-shaped phosphate. |
| 学科主题 | Chemistry, Applied ; Materials Science, Coatings & Films |
| 语种 | 英语 |
| 资助机构 | National Basic Research Program of China [2014CB643304]; Key Technology of Corrosion Control on Wind Power Equipment Academician Workstation Project [2013B090400023]; Guangzhou Industry University Research Collaborative Innovation Alliance Special Subject [201604046014] |
| 公开日期 | 2018-06-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/79623]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Liu, FC (reprint author), Chinese Acad Sci, Key Lab Nucl Mat & Safety Assessment, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Xu, L,Liu, FC,Wang, ZY,et al. The effect of surface modification of zinc particles with phosphoric acid on the corrosion resistance of cold galvanizing coatings[J]. PROGRESS IN ORGANIC COATINGS,2018,114:90-101. |
| APA | Xu, L.,Liu, FC.,Wang, ZY.,Ke, W.,Han, EH.,...&Liu, FC .(2018).The effect of surface modification of zinc particles with phosphoric acid on the corrosion resistance of cold galvanizing coatings.PROGRESS IN ORGANIC COATINGS,114,90-101. |
| MLA | Xu, L,et al."The effect of surface modification of zinc particles with phosphoric acid on the corrosion resistance of cold galvanizing coatings".PROGRESS IN ORGANIC COATINGS 114(2018):90-101. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。