Effect of carbon on the microstructure and stress rupture properties of a new Ni-Cr-W-Fe alloy for advanced ultra-supercritical power plants
文献类型：期刊论文
| 作者 | Ou, MQ; Hao, XC; Ma, YC; Liu, RC; Zhang, L; Liu, K; Ma, YC (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China. |
| 刊名 | JOURNAL OF ALLOYS AND COMPOUNDS
 |
| 出版日期 | 2018-01-25 |
| 卷号 | 732页码:107-115 |
| 关键词 | Grain-boundary Serration Nickel-based Superalloy Base Superalloy Inconel Alloy-740 Creep-properties Carbides Deformation Evolution Behavior Precipitation |
| ISSN号 | 0925-8388 |
| 英文摘要 | This paper studied the effect of carbon on the microstructure and stress rupture properties of a new Ni-Cr-W-Fe alloy. With carbon content increasing from 0.008 wt% to 0.073 wt%, the volume fraction and average size of MC and M23C6 carbides increased significantly. The morphology of MC remained dispersed blocky shape while the morphology of M23C6 changed from continuous thin strip to granular. But no obvious variations were observed in the quantity, size and morphology of gamma ' phase. During heat treatment, the hot-rolled grains grew up quickly and the grain growth rate of 0.008% C alloy was almost three times higher than that of 0.073% C alloy. The reason was that the MC carbides effectively inhibited the grain growth. After stress rupture test at 750 degrees C/300 MPa and 750 degrees C/400 MPa, the stress rupture life was in parabolic curve relationship with carbon content, 0.034 wt% and 0.045 wt% C alloys had higher stress rupture lives than other alloys. With the increase of carbon content, the ductility increased firstly and then reached relatively stable status, the fracture mode gradually varied from intergranular fracture to intergranular dimple mixed fracture. The change of stress rupture properties with carbon content was closely related to carbides and the grain size, which would be analyzed in this paper. (c) 2017 Elsevier B.V. All rights reserved.; This paper studied the effect of carbon on the microstructure and stress rupture properties of a new Ni-Cr-W-Fe alloy. With carbon content increasing from 0.008 wt% to 0.073 wt%, the volume fraction and average size of MC and M23C6 carbides increased significantly. The morphology of MC remained dispersed blocky shape while the morphology of M23C6 changed from continuous thin strip to granular. But no obvious variations were observed in the quantity, size and morphology of gamma ' phase. During heat treatment, the hot-rolled grains grew up quickly and the grain growth rate of 0.008% C alloy was almost three times higher than that of 0.073% C alloy. The reason was that the MC carbides effectively inhibited the grain growth. After stress rupture test at 750 degrees C/300 MPa and 750 degrees C/400 MPa, the stress rupture life was in parabolic curve relationship with carbon content, 0.034 wt% and 0.045 wt% C alloys had higher stress rupture lives than other alloys. With the increase of carbon content, the ductility increased firstly and then reached relatively stable status, the fracture mode gradually varied from intergranular fracture to intergranular dimple mixed fracture. The change of stress rupture properties with carbon content was closely related to carbides and the grain size, which would be analyzed in this paper. (c) 2017 Elsevier B.V. All rights reserved. |
| 学科主题 | Chemistry, Physical ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 公开日期 | 2018-06-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/79566]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Ma, YC (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Ou, MQ,Hao, XC,Ma, YC,et al. Effect of carbon on the microstructure and stress rupture properties of a new Ni-Cr-W-Fe alloy for advanced ultra-supercritical power plants[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2018,732:107-115. |
| APA | Ou, MQ.,Hao, XC.,Ma, YC.,Liu, RC.,Zhang, L.,...&Ma, YC .(2018).Effect of carbon on the microstructure and stress rupture properties of a new Ni-Cr-W-Fe alloy for advanced ultra-supercritical power plants.JOURNAL OF ALLOYS AND COMPOUNDS,732,107-115. |
| MLA | Ou, MQ,et al."Effect of carbon on the microstructure and stress rupture properties of a new Ni-Cr-W-Fe alloy for advanced ultra-supercritical power plants".JOURNAL OF ALLOYS AND COMPOUNDS 732(2018):107-115. |