Characteristics of Oxidation and Oxygen Penetration of Alloy 690 in 600 degrees C Aerated Supercritical Water
文献类型：期刊论文
| 作者 | Zhong, XY; Wu, XQ; Han, EH; Zhong, XY (reprint author), Chinese Acad Sci, Inst Met Res, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China. |
| 刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2018-03-01 |
| 卷号 | 34期号:3页码:561-569 |
| 关键词 | High-temperature Water Nickel-base Alloys Stress-corrosion Cracking Surface Oxide-films Intergranular Oxidation Elevated-temperatures Electron-microscopy Internal Oxidation Chromium Alloys Behavior |
| ISSN号 | 1005-0302 |
| 英文摘要 | The oxide films formed on Alloy 690 exposed to 600 degrees C supercritical water were characterized using mass measurement, X-ray diffraction, Raman spectroscopy, scanning electron microscopy equipped with energy dispersive X-ray spectroscopy and X-ray photoelectron spectroscopy. It was found that the mass gain of the alloy in supercritical water decreased with increasing exposure time. The oxide films have a double-layer structure, with an inner layer rich in Cr and outer layer rich in Ni and Fe after short time and long time exposure. The penetration of the oxide along the grain boundaries was observed, and the penetration depth increased with increasing exposure time. The grain boundaries and voids are the short-path of oxygen diffusion into the metal. (C) 2016 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.; The oxide films formed on Alloy 690 exposed to 600 degrees C supercritical water were characterized using mass measurement, X-ray diffraction, Raman spectroscopy, scanning electron microscopy equipped with energy dispersive X-ray spectroscopy and X-ray photoelectron spectroscopy. It was found that the mass gain of the alloy in supercritical water decreased with increasing exposure time. The oxide films have a double-layer structure, with an inner layer rich in Cr and outer layer rich in Ni and Fe after short time and long time exposure. The penetration of the oxide along the grain boundaries was observed, and the penetration depth increased with increasing exposure time. The grain boundaries and voids are the short-path of oxygen diffusion into the metal. (C) 2016 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| 学科主题 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 资助机构 | Science and Technology Foundation of China [51671201, 51371174]; Science and Technology Project of Yunnan Province; Technology Development (Cooperation) Fund from Yunnan Wenshan Dounan Manganese Industry Co., Ltd.; Innovation Fund of Institute of Metal Research (IMR), Chinese Academy of Sciences (CAS) |
| 公开日期 | 2018-06-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/79449]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zhong, XY (reprint author), Chinese Acad Sci, Inst Met Res, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Zhong, XY,Wu, XQ,Han, EH,et al. Characteristics of Oxidation and Oxygen Penetration of Alloy 690 in 600 degrees C Aerated Supercritical Water[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2018,34(3):561-569. |
| APA | Zhong, XY,Wu, XQ,Han, EH,&Zhong, XY .(2018).Characteristics of Oxidation and Oxygen Penetration of Alloy 690 in 600 degrees C Aerated Supercritical Water.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,34(3),561-569. |
| MLA | Zhong, XY,et al."Characteristics of Oxidation and Oxygen Penetration of Alloy 690 in 600 degrees C Aerated Supercritical Water".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 34.3(2018):561-569. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。