Deposition of Phase-pure Cr2AlC Coating by DC Magnetron Sputtering and Post Annealing Using Cr-Al-C Targets with Controlled Elemental Composition but Different Phase Compositions
文献类型：期刊论文
| 作者 | Li, YM; Zhao, GR; Qian, YH; Xu, JJ; Li, MS; Li, MS (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Liaoning, Peoples R China. |
| 刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2018-03-01 |
| 卷号 | 34期号:3页码:466-471 |
| 关键词 | Thin-films Oxygen Incorporation m(n+1)Ax(n) Phases Elastic Properties Oxidation Microstructure Temperature Ti3sic2 Growth Crystallization |
| ISSN号 | 1005-0302 |
| 英文摘要 | Polycrystalline Cr2AlC coatings were prepared on M38G superalloy using a two-step method consisting of magnetron sputtering from Cr-Al-C composite targets at room temperature and subsequent annealing at 620 degrees C. Particularly, various targets synthesized by hot pressing mixture of Cr, Al, and C powders at 650-1000 degrees C were used. It was found that regardless of the phase compositions and density of the composite targets, when the molar ratio of Cr:Al:C in the starting materials was 2:1:1, phase-pure crystalline Cr2AlC coatings were prepared by magnetron sputtering and post crystallization. The Cr2AlC coatings were dense and crack-free and had a duplex structure. The adhesion strength of the coating deposited on M38G superalloy from the 800 degrees C hot-pressed target and then annealed at 620 degrees C for 20 h in Ar exceeded 82 + 6 MPa, while its hardness was 12 +/- 3 GPa. (C) 2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.; Polycrystalline Cr2AlC coatings were prepared on M38G superalloy using a two-step method consisting of magnetron sputtering from Cr-Al-C composite targets at room temperature and subsequent annealing at 620 degrees C. Particularly, various targets synthesized by hot pressing mixture of Cr, Al, and C powders at 650-1000 degrees C were used. It was found that regardless of the phase compositions and density of the composite targets, when the molar ratio of Cr:Al:C in the starting materials was 2:1:1, phase-pure crystalline Cr2AlC coatings were prepared by magnetron sputtering and post crystallization. The Cr2AlC coatings were dense and crack-free and had a duplex structure. The adhesion strength of the coating deposited on M38G superalloy from the 800 degrees C hot-pressed target and then annealed at 620 degrees C for 20 h in Ar exceeded 82 + 6 MPa, while its hardness was 12 +/- 3 GPa. (C) 2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| 学科主题 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 资助机构 | National Natural Science Foundation of China [51271191, 51571205, 51401209] |
| 公开日期 | 2018-06-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/79447]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Li, MS (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Liaoning, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Li, YM,Zhao, GR,Qian, YH,et al. Deposition of Phase-pure Cr2AlC Coating by DC Magnetron Sputtering and Post Annealing Using Cr-Al-C Targets with Controlled Elemental Composition but Different Phase Compositions[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2018,34(3):466-471. |
| APA | Li, YM,Zhao, GR,Qian, YH,Xu, JJ,Li, MS,&Li, MS .(2018).Deposition of Phase-pure Cr2AlC Coating by DC Magnetron Sputtering and Post Annealing Using Cr-Al-C Targets with Controlled Elemental Composition but Different Phase Compositions.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,34(3),466-471. |
| MLA | Li, YM,et al."Deposition of Phase-pure Cr2AlC Coating by DC Magnetron Sputtering and Post Annealing Using Cr-Al-C Targets with Controlled Elemental Composition but Different Phase Compositions".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 34.3(2018):466-471. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。