Effect of cooling rate on microstructure, microsegregation and mechanical properties of cast Ni-based superalloy K417G
文献类型：期刊论文
| 作者 | Gong, L; Chen, B; Zhang, L; Ma, YC; Liu, K; Chen, B (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China. |
| 刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
 |
| 出版日期 | 2018-05-01 |
| 卷号 | 34期号:5页码:811-820 |
| 关键词 | Nickel-based Superalloys Solidification Parameters Tensile Behavior Stress Rupture Segregation Evolution Deformation Porosity Turbine |
| ISSN号 | 1005-0302 |
| 英文摘要 | The effects of different solidification rates after pouring on the microstructures, microsegregation and mechanical properties of cast superalloy K417G were investigated. Scheil-model was applied to calculate the temperature range of solidification. The casting mould with different casting runners was designed to obtain three different cooling rates. The microstructures were observed and the microsegregation was investigated. Also, high temperature tensile test was performed at 900 degrees C and stress rupture test was performed at 950 degrees C with the stress of 235 MPa. The results showed that the secondary dendrite arm spacing, microsegregation, the size and volume fraction of gamma' phase and the size of gamma/gamma' eutectic increased with decreasing cooling rate, but the volume fraction of gamma/gamma' eutectic decreased. In the cooling rate range of 1.42 degrees C s(-1)-0.84 degrees C s(-1), the cast micro-porosities and carbides varied little, while the volume fraction and size of gamma' phase and gamma/gamma' eutectic played a decisive role on mechanical properties. The specimen with the slowest cooling rate of 0.84 degrees C s(-1)showed the best comprehensive mechanical properties. (C) 2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.; The effects of different solidification rates after pouring on the microstructures, microsegregation and mechanical properties of cast superalloy K417G were investigated. Scheil-model was applied to calculate the temperature range of solidification. The casting mould with different casting runners was designed to obtain three different cooling rates. The microstructures were observed and the microsegregation was investigated. Also, high temperature tensile test was performed at 900 degrees C and stress rupture test was performed at 950 degrees C with the stress of 235 MPa. The results showed that the secondary dendrite arm spacing, microsegregation, the size and volume fraction of gamma' phase and the size of gamma/gamma' eutectic increased with decreasing cooling rate, but the volume fraction of gamma/gamma' eutectic decreased. In the cooling rate range of 1.42 degrees C s(-1)-0.84 degrees C s(-1), the cast micro-porosities and carbides varied little, while the volume fraction and size of gamma' phase and gamma/gamma' eutectic played a decisive role on mechanical properties. The specimen with the slowest cooling rate of 0.84 degrees C s(-1)showed the best comprehensive mechanical properties. (C) 2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| 学科主题 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 公开日期 | 2018-06-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/79333]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Chen, B (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Gong, L,Chen, B,Zhang, L,et al. Effect of cooling rate on microstructure, microsegregation and mechanical properties of cast Ni-based superalloy K417G[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2018,34(5):811-820. |
| APA | Gong, L,Chen, B,Zhang, L,Ma, YC,Liu, K,&Chen, B .(2018).Effect of cooling rate on microstructure, microsegregation and mechanical properties of cast Ni-based superalloy K417G.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,34(5),811-820. |
| MLA | Gong, L,et al."Effect of cooling rate on microstructure, microsegregation and mechanical properties of cast Ni-based superalloy K417G".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 34.5(2018):811-820. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。