Combined strengthening from nanotwins and nanoprecipitates in an iron-based superalloy
文献类型：期刊论文
| 作者 | Zhang, BB; Yan, FK; Zhao, MJ; Tao, NR; Lu, K; Tao, NR (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Liaoning, Peoples R China. |
| 刊名 | ACTA MATERIALIA
 |
| 出版日期 | 2018-06-01 |
| 卷号 | 151页码:310-320 |
| 关键词 | High Electrical-conductivity Dynamic Plastic-deformation Austenitic Stainless-steel Low-carbon Steels Cu-al Alloy Cr-zr Alloy Microstructural Evolution Tensile Behavior Pure Nickel Ag Alloy |
| ISSN号 | 1359-6454 |
| 英文摘要 | A bulk nanostructured solutionized iron-based superalloy consisting of nanotwins and dislocation structures was prepared by means of dynamic plastic deformation at a high strain rate. The nanotwins constitute similar to 51% in volume with the average twin/matrix lamella thickness of similar to 20 nm. The sample exhibits a yield strength as high as 1130 MPa but with nearly zero uniform elongation. Subsequent peak-aging treatment at 700 degrees C for 1 h results in the precipitation of nano-sized gamma prime phases with a random distribution in the nanotwins and deformed matrix. The nanotwins still remain and keep the corresponding strengthening after aging. Those dispersed nanoprecipitates further raise the strength of the aged sample to 1420 MPa. Meanwhile, the uniform elongation increases to similar to 3% due to the intrinsic plasticity of nanotwins with a reduced dislocation density after aging annealing. This kind of combined strengthening from both nanotwins and precipitates provides a new strategy to further raise the strength of nanotwinned materials or precipitation-strengthened materials. (C) 2018 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.; A bulk nanostructured solutionized iron-based superalloy consisting of nanotwins and dislocation structures was prepared by means of dynamic plastic deformation at a high strain rate. The nanotwins constitute similar to 51% in volume with the average twin/matrix lamella thickness of similar to 20 nm. The sample exhibits a yield strength as high as 1130 MPa but with nearly zero uniform elongation. Subsequent peak-aging treatment at 700 degrees C for 1 h results in the precipitation of nano-sized gamma prime phases with a random distribution in the nanotwins and deformed matrix. The nanotwins still remain and keep the corresponding strengthening after aging. Those dispersed nanoprecipitates further raise the strength of the aged sample to 1420 MPa. Meanwhile, the uniform elongation increases to similar to 3% due to the intrinsic plasticity of nanotwins with a reduced dislocation density after aging annealing. This kind of combined strengthening from both nanotwins and precipitates provides a new strategy to further raise the strength of nanotwinned materials or precipitation-strengthened materials. (C) 2018 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved. |
| 学科主题 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 资助机构 | National Natural Science Foundation of China [51771196, 51501191, U1730140]; National Key R&D Program of China [2017YFA0204401, 2017YFA0204402]; Key Research Program of Frontier Science, Chinese Academy of Sciences |
| 公开日期 | 2018-06-05 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/79290]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Tao, NR (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Liaoning, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Zhang, BB,Yan, FK,Zhao, MJ,et al. Combined strengthening from nanotwins and nanoprecipitates in an iron-based superalloy[J]. ACTA MATERIALIA,2018,151:310-320. |
| APA | Zhang, BB,Yan, FK,Zhao, MJ,Tao, NR,Lu, K,&Tao, NR .(2018).Combined strengthening from nanotwins and nanoprecipitates in an iron-based superalloy.ACTA MATERIALIA,151,310-320. |
| MLA | Zhang, BB,et al."Combined strengthening from nanotwins and nanoprecipitates in an iron-based superalloy".ACTA MATERIALIA 151(2018):310-320. |