New insights into the effect of Tris-HCl and Tris on corrosion of magnesium alloy in presence of bicarbonate, sulfate, hydrogen phosphate and dihydrogen phosphate ions
文献类型：期刊论文
| 作者 | Cui, Lan-Yue; Hu, Yan; Zeng, Rong-Chang; Yang, Yong-Xin; Sun, Dan-Dan; Li, Shuo-Qi; Zhang, Fen; Han, En-Hou; Zeng, RC (reprint author), Shandong Univ Sci & Technol, Coll Mat Sci & Engn, Qingdao 266590, Peoples R China. |
| 刊名 | JOURNAL MATER SCI TECHNOL
 |
| 出版日期 | 2017-09-01 |
| 卷号 | 33期号:9页码:971-986 |
| ISSN号 | 1005-0302 |
| 关键词 | Magnesium Alloy Biomaterials Tris Buffer Corrosion |
| 英文摘要 | In vitro degradation is an important approach to screening appropriate biomedical magnesium (Mg) alloys at low cost. However, corrosion products deposited on Mg alloys exert a critical impact on corrosion resistance. There are no acceptable criteria on the evaluation on degradation rate of Mg alloys. Understanding the degradation behavior of Mg alloys in presence of Tris buffer is necessary. An investigation was made to compare the influence of Tris-HCl and Tris on the corrosion behavior of Mg alloy AZ31 in the presence of various anions of simulated body fluids via hydrogen evolution, pH value and electrochemical tests. The results demonstrated that the Tris-HCl buffer resulted in general corrosion due to the inhibition of the formation of corrosion products and thus increased the corrosion rate of the AZ31 alloy. Whereas Tris gave rise to pitting corrosion or general corrosion due to the fact that the hydrolysis of the amino-group of Tris led to an increase in solution pH value, and promoted the formation of corrosion products and thus a significant reduction in corrosion rate. In addition, the corrosion mechanisms in the presence of Tris-HCl and Tris were proposed. Tris-HCl as a buffer prevented the formation of precipitates of HCO3-, SO42-, HPO42- and H2PO4- ions during the corrosion of the AZ31 alloy due to its lower buffering pH value (x. x). Thus, both the hydrogen evolution rate and corrosion current density of the alloy were approximately one order of magnitude higher in presence of Tris-HCl than Tris and Tris-free saline solutions. (C) 2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.; In vitro degradation is an important approach to screening appropriate biomedical magnesium (Mg) alloys at low cost. However, corrosion products deposited on Mg alloys exert a critical impact on corrosion resistance. There are no acceptable criteria on the evaluation on degradation rate of Mg alloys. Understanding the degradation behavior of Mg alloys in presence of Tris buffer is necessary. An investigation was made to compare the influence of Tris-HCl and Tris on the corrosion behavior of Mg alloy AZ31 in the presence of various anions of simulated body fluids via hydrogen evolution, pH value and electrochemical tests. The results demonstrated that the Tris-HCl buffer resulted in general corrosion due to the inhibition of the formation of corrosion products and thus increased the corrosion rate of the AZ31 alloy. Whereas Tris gave rise to pitting corrosion or general corrosion due to the fact that the hydrolysis of the amino-group of Tris led to an increase in solution pH value, and promoted the formation of corrosion products and thus a significant reduction in corrosion rate. In addition, the corrosion mechanisms in the presence of Tris-HCl and Tris were proposed. Tris-HCl as a buffer prevented the formation of precipitates of HCO3-, SO42-, HPO42- and H2PO4- ions during the corrosion of the AZ31 alloy due to its lower buffering pH value (x. x). Thus, both the hydrogen evolution rate and corrosion current density of the alloy were approximately one order of magnitude higher in presence of Tris-HCl than Tris and Tris-free saline solutions. (C) 2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
| 学科主题 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 资助机构 | National Natural Science Foundation of China [51241001, 51571134]; SDUST Research Fund [2014TDJH104]; Joint Innovative Centre for Safe and Effective Mining Technology and Equipment of Coal Resources, Shandong Province |
| 公开日期 | 2018-01-10 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/79117]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zeng, RC (reprint author), Shandong Univ Sci & Technol, Coll Mat Sci & Engn, Qingdao 266590, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Cui, Lan-Yue,Hu, Yan,Zeng, Rong-Chang,et al. New insights into the effect of Tris-HCl and Tris on corrosion of magnesium alloy in presence of bicarbonate, sulfate, hydrogen phosphate and dihydrogen phosphate ions[J]. JOURNAL MATER SCI TECHNOL,2017,33(9):971-986. |
| APA | Cui, Lan-Yue.,Hu, Yan.,Zeng, Rong-Chang.,Yang, Yong-Xin.,Sun, Dan-Dan.,...&Zeng, RC .(2017).New insights into the effect of Tris-HCl and Tris on corrosion of magnesium alloy in presence of bicarbonate, sulfate, hydrogen phosphate and dihydrogen phosphate ions.JOURNAL MATER SCI TECHNOL,33(9),971-986. |
| MLA | Cui, Lan-Yue,et al."New insights into the effect of Tris-HCl and Tris on corrosion of magnesium alloy in presence of bicarbonate, sulfate, hydrogen phosphate and dihydrogen phosphate ions".JOURNAL MATER SCI TECHNOL 33.9(2017):971-986. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。