Relationship Between pH and Electrochemical Corrosion Behavior of Thermal-Sprayed Ni-Al-Coated Q235 Steel in Simulated Soil Solutions
文献类型：期刊论文
| 作者 | Wei, Wei; Wu, Xin-qiang; Ke, Wei; Xu, Song; Feng, Bing; Hu, Bo-tao; Wu, XQ (reprint author), Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, Shenyang 110016, Liaoning, Peoples R China. |
| 刊名 | SPRINGER
 |
| 出版日期 | 2017-09-01 |
| 卷号 | 26期号:9页码:4340-4348 |
| 关键词 | Corrosion Resistance Grounding Grids Ni-al Coating Ph Value Thermal Spraying |
| ISSN号 | 1059-9495 |
| 英文摘要 | Electrochemical corrosion behavior of a thermal-sprayed Ni-Al-coated Q235 steel was investigated in the simulated soil solutions at different pH values using measurements of potentiodynamic polarization curves and electrochemical impedance spectroscopy as well as surface analyses including x-ray diffraction analysis, scanning electron microscope equipped with an energy-dispersive x-ray spectroscopy and x-ray photoelectron spectroscopy. The results showed that the corrosion resistance of the Ni-Al-coated Q235 steel was dependent on the pH of the test solution. From pH = 3.53 to pH = 4.79, the corrosion resistance of the coated steel increased rapidly. In the pH range from 4.79 to 12.26, the corrosion resistance exhibited no significant change. At pH 13.25, the corrosion resistance of the sample was found to decrease. The calculated corrosion rate of Ni-Al-coated Q235 steel was lower than that of the uncoated Q235 steel and galvanized steel in all the test solutions. Over a wide range of pH values, the Ni-Al-coated Q235 steel exhibited extremely good corrosion resistance. The experimental data together with the potential-pH diagrams provided a basis for a detailed discussion of the related corrosion mechanisms of the coated steel.; Electrochemical corrosion behavior of a thermal-sprayed Ni-Al-coated Q235 steel was investigated in the simulated soil solutions at different pH values using measurements of potentiodynamic polarization curves and electrochemical impedance spectroscopy as well as surface analyses including x-ray diffraction analysis, scanning electron microscope equipped with an energy-dispersive x-ray spectroscopy and x-ray photoelectron spectroscopy. The results showed that the corrosion resistance of the Ni-Al-coated Q235 steel was dependent on the pH of the test solution. From pH = 3.53 to pH = 4.79, the corrosion resistance of the coated steel increased rapidly. In the pH range from 4.79 to 12.26, the corrosion resistance exhibited no significant change. At pH 13.25, the corrosion resistance of the sample was found to decrease. The calculated corrosion rate of Ni-Al-coated Q235 steel was lower than that of the uncoated Q235 steel and galvanized steel in all the test solutions. Over a wide range of pH values, the Ni-Al-coated Q235 steel exhibited extremely good corrosion resistance. The experimental data together with the potential-pH diagrams provided a basis for a detailed discussion of the related corrosion mechanisms of the coated steel. |
| 学科主题 | Materials Science, Multidisciplinary |
| 语种 | 英语 |
| 资助机构 | Science and Technology Foundation of China [51371174]; Science Project of State Grid Corporation of China [KG12K16004]; Innovation Fund of IMR, CAS |
| 公开日期 | 2018-01-10 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/79111]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wu, XQ (reprint author), Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, Shenyang 110016, Liaoning, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Wei, Wei,Wu, Xin-qiang,Ke, Wei,et al. Relationship Between pH and Electrochemical Corrosion Behavior of Thermal-Sprayed Ni-Al-Coated Q235 Steel in Simulated Soil Solutions[J]. SPRINGER,2017,26(9):4340-4348. |
| APA | Wei, Wei.,Wu, Xin-qiang.,Ke, Wei.,Xu, Song.,Feng, Bing.,...&Wu, XQ .(2017).Relationship Between pH and Electrochemical Corrosion Behavior of Thermal-Sprayed Ni-Al-Coated Q235 Steel in Simulated Soil Solutions.SPRINGER,26(9),4340-4348. |
| MLA | Wei, Wei,et al."Relationship Between pH and Electrochemical Corrosion Behavior of Thermal-Sprayed Ni-Al-Coated Q235 Steel in Simulated Soil Solutions".SPRINGER 26.9(2017):4340-4348. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。