Corrosion Behavior of Cu40Zn in Sulfide-Polluted 3.5% NaCl Solution
文献类型:期刊论文
作者 | Song, Q. N.; Xu, N.; Bao, Y. F.; Jiang, Y. F.; Gu, W.; Yang, Z.; Zheng, Y. G.; Qiao, Y. X.; Bao, YF (reprint author), Hohai Univ, Coll Mech & Elect Engn, 200 Jinling North Rd, Changzhou 213022, Peoples R China. |
刊名 | SPRINGER |
出版日期 | 2017-10-01 |
卷号 | 26期号:10页码:4822-4830 |
ISSN号 | 1059-9495 |
关键词 | Corrosion Product Film Electrochemical Measurements Nonferrous Metals Sulfide X-ray |
英文摘要 | The corrosion behavior of a duplex-phase brass Cu40Zn in clean and sulfide-polluted 3.5% NaCl solutions was investigated by conducting electrochemical and gravimetric measurements. The corrosion product films were analyzed by scanning electron microscopy, energy-dispersive spectroscopy and x-ray diffraction. The presence of sulfide shifted the corrosion potential of Cu40Zn toward a more negative value by 100 mV and increased the mass loss rate by a factor of 1.257 compared with the result in the clean solution. The corrosion product film in the clean solution was thin and compact; it mainly consisted of oxides, such as ZnO and Cu2O. By contrast, the film in the sulfide-polluted solution was thick and porous. It mainly contained sulfides and zinc hydroxide chloride (i.e., Zn-5(OH)(8)Cl-2 center dot H2O). The presence of sulfide ions accelerated the corrosion damage of Cu40Zn by hindering the formation of protective oxides and promoting the formation of a defective film which consisted of sulfides and hydroxide chlorides.; The corrosion behavior of a duplex-phase brass Cu40Zn in clean and sulfide-polluted 3.5% NaCl solutions was investigated by conducting electrochemical and gravimetric measurements. The corrosion product films were analyzed by scanning electron microscopy, energy-dispersive spectroscopy and x-ray diffraction. The presence of sulfide shifted the corrosion potential of Cu40Zn toward a more negative value by 100 mV and increased the mass loss rate by a factor of 1.257 compared with the result in the clean solution. The corrosion product film in the clean solution was thin and compact; it mainly consisted of oxides, such as ZnO and Cu2O. By contrast, the film in the sulfide-polluted solution was thick and porous. It mainly contained sulfides and zinc hydroxide chloride (i.e., Zn-5(OH)(8)Cl-2 center dot H2O). The presence of sulfide ions accelerated the corrosion damage of Cu40Zn by hindering the formation of protective oxides and promoting the formation of a defective film which consisted of sulfides and hydroxide chlorides. |
学科主题 | Materials Science, Multidisciplinary |
语种 | 英语 |
资助机构 | National Natural Science Foundation of China [51601058]; Fundamental Research Funds for the Central Universities of P.R. China [2015B30314, 2014B11614] |
公开日期 | 2018-01-10 |
源URL | [http://ir.imr.ac.cn/handle/321006/79065] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Bao, YF (reprint author), Hohai Univ, Coll Mech & Elect Engn, 200 Jinling North Rd, Changzhou 213022, Peoples R China. |
推荐引用方式 GB/T 7714 | Song, Q. N.,Xu, N.,Bao, Y. F.,et al. Corrosion Behavior of Cu40Zn in Sulfide-Polluted 3.5% NaCl Solution[J]. SPRINGER,2017,26(10):4822-4830. |
APA | Song, Q. N..,Xu, N..,Bao, Y. F..,Jiang, Y. F..,Gu, W..,...&Bao, YF .(2017).Corrosion Behavior of Cu40Zn in Sulfide-Polluted 3.5% NaCl Solution.SPRINGER,26(10),4822-4830. |
MLA | Song, Q. N.,et al."Corrosion Behavior of Cu40Zn in Sulfide-Polluted 3.5% NaCl Solution".SPRINGER 26.10(2017):4822-4830. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。