The creep deformation and fracture behaviors of nickel-base superalloy M951G at 900 degrees C
文献类型：期刊论文
| 作者 | Cui, Luqing; Su, Huhu; Yu, Jinjiang; Liu, Jinlai; Jin, Tao; Sun, Xiaofeng; Yu, JJ (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China. |
| 刊名 | ELSEVIER SCIENCE SA
 |
| 出版日期 | 2017-11-07 |
| 卷号 | 707页码:383-391 |
| 关键词 | M951g Alloy Stress Level Creep Behavior Deformation Mechanism Creep Fracture Mode |
| ISSN号 | 0921-5093 |
| 英文摘要 | The creep behaviors of M951G alloy were carried out under stress ranging from 240 MPa to 400 MPa at 900 degrees C, and the corresponding deformation mechanisms and fracture behaviors after rupture had been investigated by various techniques. Results showed that both the deformation mechanisms and fracture behaviors were dependent on the applied stress. According to the transmission electron microscope (TEM) observations, the dominant deformation mechanism changed from a combined process of slip and climb of dislocations in matrix channel to shearing of dislocations in gamma' precipitates and cross-slip of dislocations in matrix channel with the applied stress increasing. Fracture behaviors of M951G alloy were characterized using optical microscope (OM) and scanning electron microscope (SEM), which changed from intergranular to transgranular with the increase of applied stress. At low applied stress, M951G alloy was failure in the form of intergranular owing to coalescence of micropores along the grain boundaries. However, at higher applied stress the microcracks initiated at broken carbides in the grain interior, and finally resulted in transgranular fracture. Additionally, creep strain rate also played a key role in determining the transition of creep fracture modes by effect the corresponding temperature of equal strength for grain boundary and grain interior. The values of apparent stress exponent at low and high stress regions were calculated to be 5.14 and 11.13 respectively, which was due to the change of deformation mechanisms and fracture modes with the increase of applied stress.; The creep behaviors of M951G alloy were carried out under stress ranging from 240 MPa to 400 MPa at 900 degrees C, and the corresponding deformation mechanisms and fracture behaviors after rupture had been investigated by various techniques. Results showed that both the deformation mechanisms and fracture behaviors were dependent on the applied stress. According to the transmission electron microscope (TEM) observations, the dominant deformation mechanism changed from a combined process of slip and climb of dislocations in matrix channel to shearing of dislocations in gamma' precipitates and cross-slip of dislocations in matrix channel with the applied stress increasing. Fracture behaviors of M951G alloy were characterized using optical microscope (OM) and scanning electron microscope (SEM), which changed from intergranular to transgranular with the increase of applied stress. At low applied stress, M951G alloy was failure in the form of intergranular owing to coalescence of micropores along the grain boundaries. However, at higher applied stress the microcracks initiated at broken carbides in the grain interior, and finally resulted in transgranular fracture. Additionally, creep strain rate also played a key role in determining the transition of creep fracture modes by effect the corresponding temperature of equal strength for grain boundary and grain interior. The values of apparent stress exponent at low and high stress regions were calculated to be 5.14 and 11.13 respectively, which was due to the change of deformation mechanisms and fracture modes with the increase of applied stress. |
| 学科主题 | Nanoscience & Nanotechnology ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 资助机构 | National Natural Science Foundation of China (NSFC) [50931004, 51771191, 51571196] |
| 公开日期 | 2018-01-10 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/78983]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Yu, JJ (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Cui, Luqing,Su, Huhu,Yu, Jinjiang,et al. The creep deformation and fracture behaviors of nickel-base superalloy M951G at 900 degrees C[J]. ELSEVIER SCIENCE SA,2017,707:383-391. |
| APA | Cui, Luqing.,Su, Huhu.,Yu, Jinjiang.,Liu, Jinlai.,Jin, Tao.,...&Yu, JJ .(2017).The creep deformation and fracture behaviors of nickel-base superalloy M951G at 900 degrees C.ELSEVIER SCIENCE SA,707,383-391. |
| MLA | Cui, Luqing,et al."The creep deformation and fracture behaviors of nickel-base superalloy M951G at 900 degrees C".ELSEVIER SCIENCE SA 707(2017):383-391. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。