Effect of Heat Treatment on Microstructure and Mechanical Properties of A380 Aluminum Alloy Deposited by Cold Spray
文献类型：期刊论文
| 作者 | Qiu, Xiang; Wang, Ji-qiang; Tariq, Naeem ul Haq; Gyansah, Lawrence; Zhang, Jing-xuan; Xiong, Tian-ying; Wang, JQ; Xiong, TY (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China. |
| 刊名 | SPRINGER
 |
| 出版日期 | 2017-12-01 |
| 卷号 | 26期号:8页码:1898-1907 |
| 关键词 | Cold Spray Heat Treatment Mechanical Properties Microstructure |
| ISSN号 | 1059-9630 |
| 英文摘要 | The microstructure and mechanical properties of cold-sprayed bulk A380 alloy were investigated after heat treatment at various conditions, using optical and electron microscopy and tensile and hardness tests, respectively. The results revealed that heat treatment increased the strength and ductility of the cold-sprayed A380 alloy deposits compared with as-sprayed state. Heat treatment showed two different effects on the mechanical properties of the deposits. On the one hand, it resulted in effective diffusion at interparticle boundaries that altered the particle bonding mechanism from pure mechanical interlocking to metallurgical bonding. Thus, the strength and ductility of the material were greatly enhanced. On the other hand, interparticle diffusion during high-temperature heat treatment resulted in growth of the Si phase and pores, which ultimately reduced the strength and elongation of the alloy. This observation was consistent with the hardness results, which showed a decreasing trend with increase of the heat treatment temperature.; The microstructure and mechanical properties of cold-sprayed bulk A380 alloy were investigated after heat treatment at various conditions, using optical and electron microscopy and tensile and hardness tests, respectively. The results revealed that heat treatment increased the strength and ductility of the cold-sprayed A380 alloy deposits compared with as-sprayed state. Heat treatment showed two different effects on the mechanical properties of the deposits. On the one hand, it resulted in effective diffusion at interparticle boundaries that altered the particle bonding mechanism from pure mechanical interlocking to metallurgical bonding. Thus, the strength and ductility of the material were greatly enhanced. On the other hand, interparticle diffusion during high-temperature heat treatment resulted in growth of the Si phase and pores, which ultimately reduced the strength and elongation of the alloy. This observation was consistent with the hardness results, which showed a decreasing trend with increase of the heat treatment temperature. |
| 学科主题 | Materials Science, Coatings & Films |
| 语种 | 英语 |
| 资助机构 | National Natural Science Foundation of China [51671205] |
| 公开日期 | 2018-01-10 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/78950]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wang, JQ; Xiong, TY (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Qiu, Xiang,Wang, Ji-qiang,Tariq, Naeem ul Haq,et al. Effect of Heat Treatment on Microstructure and Mechanical Properties of A380 Aluminum Alloy Deposited by Cold Spray[J]. SPRINGER,2017,26(8):1898-1907. |
| APA | Qiu, Xiang.,Wang, Ji-qiang.,Tariq, Naeem ul Haq.,Gyansah, Lawrence.,Zhang, Jing-xuan.,...&Xiong, TY .(2017).Effect of Heat Treatment on Microstructure and Mechanical Properties of A380 Aluminum Alloy Deposited by Cold Spray.SPRINGER,26(8),1898-1907. |
| MLA | Qiu, Xiang,et al."Effect of Heat Treatment on Microstructure and Mechanical Properties of A380 Aluminum Alloy Deposited by Cold Spray".SPRINGER 26.8(2017):1898-1907. |