Influence of type and morphology of carbides on stress-rupture behavior of a cast cobalt-base superalloy
文献类型：期刊论文
| 作者 | Gui, Weimin; Zhang, Hongyu; Yang, Min; Jin, Tao; Sun, Xiaofeng; Zheng, Qi; Zheng, Q (reprint author), Chinese Acad Sci, Inst Met Res, Superalloys Div, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China. |
| 刊名 | ELSEVIER SCIENCE SA
 |
| 出版日期 | 2017-12-25 |
| 卷号 | 728页码:145-151 |
| ISSN号 | 0925-8388 |
| 关键词 | Cobalt-base Superalloy Heat Treatment Stress-rupture Carbide Phase Transformation |
| 英文摘要 | The relationships between the type and morphology of carbides and stress-rupture property have been studied in a cast cobalt-base superalloy. Different types and morphologies of carbides are achieved by varying the heat treatment conditions. After heat treatment at 1240 degrees C/4 h, the primary M7C3 decomposes into M23C6, and the formed M23C6 and primary MC partially dissolve into the matrix. After heat treatment at 1280 degrees C/4 h, the primary M7C3 melts, resulting in the formation of a highly developed lamellar structure of M23C6, and the primary MC mostly dissolves into the matrix. The heat treatment at 1100 degrees C/300 h gives rise to the carbide transformation of M7C3 -> M23C6 and a profusion of secondary M23C6 carbide around M23C6 and MC. The samples in stress-rupture test at 980 degrees C for 83 MPa manifest the following rupture life: 1280 degrees C sample > 1240 degrees C sample > as-cast sample > 1100 degrees C sample. The longer rupture life of the samples of 1240 degrees C and 1280 degrees C is derived from the stable microstructure, dispersed MC carbide morphology and the supersaturated matrix. The shortest rupture life of the 1100 degrees C sample is mainly attributed to the overaging. Additionally, the carbide transformations of M7C3 -> M23C6, MC -> M23C6, M23C6 -> M6C take place in the as-cast sample during creep exposure. (C) 2017 Elsevier B.V. All rights reserved.; The relationships between the type and morphology of carbides and stress-rupture property have been studied in a cast cobalt-base superalloy. Different types and morphologies of carbides are achieved by varying the heat treatment conditions. After heat treatment at 1240 degrees C/4 h, the primary M7C3 decomposes into M23C6, and the formed M23C6 and primary MC partially dissolve into the matrix. After heat treatment at 1280 degrees C/4 h, the primary M7C3 melts, resulting in the formation of a highly developed lamellar structure of M23C6, and the primary MC mostly dissolves into the matrix. The heat treatment at 1100 degrees C/300 h gives rise to the carbide transformation of M7C3 -> M23C6 and a profusion of secondary M23C6 carbide around M23C6 and MC. The samples in stress-rupture test at 980 degrees C for 83 MPa manifest the following rupture life: 1280 degrees C sample > 1240 degrees C sample > as-cast sample > 1100 degrees C sample. The longer rupture life of the samples of 1240 degrees C and 1280 degrees C is derived from the stable microstructure, dispersed MC carbide morphology and the supersaturated matrix. The shortest rupture life of the 1100 degrees C sample is mainly attributed to the overaging. Additionally, the carbide transformations of M7C3 -> M23C6, MC -> M23C6, M23C6 -> M6C take place in the as-cast sample during creep exposure. (C) 2017 Elsevier B.V. All rights reserved. |
| 学科主题 | Chemistry, Physical ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 资助机构 | National Natural Science Foundation of China [51331005, 51601192, 51671188, 11332010]; High Technology Research and Development Program of China [2014AA041701] |
| 公开日期 | 2018-01-10 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/78926]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zheng, Q (reprint author), Chinese Acad Sci, Inst Met Res, Superalloys Div, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Gui, Weimin,Zhang, Hongyu,Yang, Min,et al. Influence of type and morphology of carbides on stress-rupture behavior of a cast cobalt-base superalloy[J]. ELSEVIER SCIENCE SA,2017,728:145-151. |
| APA | Gui, Weimin.,Zhang, Hongyu.,Yang, Min.,Jin, Tao.,Sun, Xiaofeng.,...&Zheng, Q .(2017).Influence of type and morphology of carbides on stress-rupture behavior of a cast cobalt-base superalloy.ELSEVIER SCIENCE SA,728,145-151. |
| MLA | Gui, Weimin,et al."Influence of type and morphology of carbides on stress-rupture behavior of a cast cobalt-base superalloy".ELSEVIER SCIENCE SA 728(2017):145-151. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。