Degradation failure features of chromium-plated gun barrels with a laser-discrete-quenched substrate
文献类型：期刊论文
| 作者 | Li HX(李怀学) ; Chen GN(陈光南); Zhang K(张坤); Luo GX(罗耕星); Ye ZJ(叶智军)
|
| 刊名 | Surface & Coatings Technology
 |
| 出版日期 | 2007 |
| 卷号 | 201期号:24页码:9558-9564 |
| 通讯作者邮箱 | lhx1022@126.com |
| 关键词 | Gun Bore Electrodeposited Chromium Interface Laser-Discrete Quenching Bore Erosion Thermal-Damage Army Cannons Coatings System Mechanisms Stresses Cracking |
| ISSN号 | 0257-8972 |
| 通讯作者 | Li, HX (reprint author), Chinese Acad Sci, Inst Mech, Beijing 100080, Peoples R China. |
| 中文摘要 | The effect of substrate laser-discrete quenching on the degradation failure of chromium-plated gun barrels was metallurgically investigated. The results show that substrate laser-discrete quenching changes the failure patterns of chromium coatings during firing, and some periodic through-thickness cracks in the fired chromium coatings are justly located at original substrate zones between two adjacent laser-quenched tracks. Moreover, chromium coatings and the laser-quenched zones on the substrate are simultaneously degraded in microstructure and property during firing. Furthermore, the periodic structure of the laser-discrete-quenched steel (LDQS) substrate near the breech remains after firing, and the hardness of the fired laser-quenched zones is still higher than that of original substrates. The specific failure features were utilized to illustrate the mechanism of the extended service life of chromium-plated gun barrels with the LDQS substrate. (c) 2007 Elsevier B.V All rights reserved. |
| 类目[WOS] | Materials Science, Coatings & Films ; Physics, Applied |
| 研究领域[WOS] | Materials Science ; Physics |
| 关键词[WOS] | BORE EROSION ; THERMAL-DAMAGE ; ARMY CANNONS ; COATINGS ; SYSTEM ; MECHANISMS ; STRESSES ; CRACKING |
| 收录类别 | SCI ; EI |
| 语种 | 英语 |
| WOS记录号 | WOS:000250068500017 |
| 公开日期 | 2009-08-03 ; 2010-06-13 |
| 源URL | [http://dspace.imech.ac.cn/handle/311007/33897]  |
| 专题 | 力学研究所_力学所知识产出(1956-2008) |
| 推荐引用方式 GB/T 7714 | Li HX,Chen GN,Zhang K,et al. Degradation failure features of chromium-plated gun barrels with a laser-discrete-quenched substrate[J]. Surface & Coatings Technology,2007,201(24):9558-9564. |
| APA | 李怀学,陈光南,张坤,罗耕星,&叶智军.(2007).Degradation failure features of chromium-plated gun barrels with a laser-discrete-quenched substrate.Surface & Coatings Technology,201(24),9558-9564. |
| MLA | 李怀学,et al."Degradation failure features of chromium-plated gun barrels with a laser-discrete-quenched substrate".Surface & Coatings Technology 201.24(2007):9558-9564. |
入库方式： OAI收割
来源：力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。