Fe3O4/carbon chain-like core/shell composites: Synthesis and microwave absorption properties
文献类型:期刊论文
作者 | Wang, Shipeng1; Huang, Fei1; Zhang, Min1; Kong, Xiangkai1; Zi, Zhenfa2; Liu, Qiangchun1 |
刊名 | INTEGRATED FERROELECTRICS |
出版日期 | 2018 |
卷号 | 190期号:1页码:76-84 |
ISSN号 | 1058-4587 |
关键词 | Fe3O4 carbon composite core shell composites hydrothermal method microwave absorption |
DOI | 10.1080/10584587.2018.1456176 |
通讯作者 | Liu, Qiangchun(qchliu@chnu.edu.cn) |
英文摘要 | Fe3O4/carbon core/shell composites were fabricated via a two-step process. Fe3O4/phenol formaldehyde resin (PFR) core/shell composites were first obtained by hydrothermal method, and the Fe3O4/carbon core/shell composites were produced by annealing Fe3O4/PFR core/shell composites under nitrogen flow. The phase structures and morphologies of the composites had been characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscope (TEM). The microwave absorption properties of the Fe3O4/carbon core/shell composites were measured by vector network analysis (VNA). When the ratio of Fe3O4 and carbon is 1:2 and the sample thickness is 2.4mm, the Fe3O4/carbon core/shell composites have an optimal absorption peak value of about -45.3dB at 9.7GHz and its effective absorption bandwidth lower than -10dB reaches 2.3GHz (from 7.8 to 11.1GHz). The reflection loss results indicate that the Fe3O4/carbon core/shell composites possess higher microwave absorption. The excellent electromagnetic wave absorption properties of the Fe3O4/carbon core/shell composites were attributed to effective complementarities between the dielectric loss and the magnetic loss. |
WOS关键词 | ELECTROMAGNETIC-WAVE ABSORPTION ; SHELL MICROSPHERES ; CARBON NANOTUBES ; ABSORBERS |
WOS研究方向 | Engineering ; Physics |
语种 | 英语 |
出版者 | TAYLOR & FRANCIS LTD |
WOS记录号 | WOS:000442004300011 |
源URL | [http://ir.hfcas.ac.cn:8080/handle/334002/38067] |
专题 | 合肥物质科学研究院_中科院固体物理研究所 |
通讯作者 | Liu, Qiangchun |
作者单位 | 1.Huaibei Normal Univ, Collaborat Innovat Ctr Adv Funct Composites, Huaibei, Peoples R China 2.Chinese Acad Sci, Inst Solid State Phys, Key Lab Mat Phys, Hefei, Anhui, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Shipeng,Huang, Fei,Zhang, Min,et al. Fe3O4/carbon chain-like core/shell composites: Synthesis and microwave absorption properties[J]. INTEGRATED FERROELECTRICS,2018,190(1):76-84. |
APA | Wang, Shipeng,Huang, Fei,Zhang, Min,Kong, Xiangkai,Zi, Zhenfa,&Liu, Qiangchun.(2018).Fe3O4/carbon chain-like core/shell composites: Synthesis and microwave absorption properties.INTEGRATED FERROELECTRICS,190(1),76-84. |
MLA | Wang, Shipeng,et al."Fe3O4/carbon chain-like core/shell composites: Synthesis and microwave absorption properties".INTEGRATED FERROELECTRICS 190.1(2018):76-84. |
入库方式: OAI收割
来源:合肥物质科学研究院
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。