Investigations of nano-defect morphology and vibrational spectra of swift heavy ion irradiated muscovite mica
文献类型：会议论文
| 作者 | Zhang, S. X.1; Liu, J.1 ; Hu, P. P.1,2; Zeng, J.1; Maaz, K.1; Zhai, P. F.1; Duan, J. L.1; Yao, H. J.1; Sun, Y. M.1; Hou, M. D.1
|
| 出版日期 | 2018-12-15 |
| 关键词 | Muscovite mica Swift heavy ion irradiation Nano-defects Vibrational mode |
| 卷号 | 355 |
| DOI | 10.1016/j.surfcoat.2018.04.033 |
| 页码 | 186-190 |
| 英文摘要 | Muscovite mica sheets with a thickness of 12 mu m were irradiated by various kinds of swift heavy ions in Heavy Ion Research Facility in Lanzhou (HIRFL). During the irradiation process, the fluence was kept in the range 1 x 10(10) -1 x 10(12) ions/cm(2), whereas the electronic stopping power S-e was in the range from 5.9 to 31.5 keV/nm. The vibrational modifications in irradiated mica were investigated by Fourier-transform infrared (FTIR) spectroscopy and the morphology of the nano-defects on the surface of mica was analyzed by the atomic force microscopy (AFM) in the tapping mode. The infrared spectrum showed that motions from all atomic types in the muscovite mica structure could be found in modes for all vibrations. The intensity of all observed vibrational modes, including the O-H stretching motion at 3621 cm(-1), was found to decrease with increasing S, values and ion fluences. It was indicated that formation of the defects and structural modifications take place in muscovite mica as a result of swift heavy ion irradiation, and it was found that more defects were introduced in mica by irradiation with higher ion fluences and higher electronic stopping power S, values. The morphology of nano defects on the surface of mica that depends on the applied S, was discussed in detail this work. Craters were observed in the samples irradiated by Xe ions with electronic stopping power of 21.8 keV/nm or by Bi ions with electronic stopping power of 31.5 keV/nm. While the hillocks with craters on the top were found on the surface of mica irradiated by Kr ions with S, values of 9.0 keV/nm. |
| 会议录 | SURFACE & COATINGS TECHNOLOGY
 |
| 会议录出版者 | ELSEVIER SCIENCE SA |
| 会议录出版地 | PO BOX 564, 1001 LAUSANNE, SWITZERLAND |
| 语种 | 英语 |
| 资助项目 | Outstanding Young Scientist Project, Key Research Program of Frontier Sciences, CAS[QYZDB-SSW-SLH010] |
| WOS研究方向 | Materials Science ; Physics |
| WOS记录号 | WOS:000449896800029 |
| 源URL | [http://119.78.100.186/handle/113462/63974]  |
| 专题 | 中国科学院近代物理研究所 |
| 通讯作者 | Zhang, S. X.; Liu, J. |
| 作者单位 | 1.Chinese Acad Sci, Inst Modern Phys, Lanzhou 730000, Gansu, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, S. X.,Liu, J.,Hu, P. P.,et al. Investigations of nano-defect morphology and vibrational spectra of swift heavy ion irradiated muscovite mica[C]. 见:. |
入库方式： OAI收割
来源：近代物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。