Nanoindentation on V-4Ti alloy irradiated by H and He ions

文献类型：期刊论文

作者Song, Y1; Yang, YT1; Zhang, CH1; Gou, J1; Liu, J2; Meng, YC1; Xian, YQ2
刊名JOURNAL OF NUCLEAR MATERIALS
出版日期2015
卷号459期号:459页码:1-4
ISSN号0022-3115
DOI10.1016/j.jnucmat.2015.01.020
英文摘要V-4Ti and V samples were irradiated by H/He ions with various energies to produce a damage plateau in the region from surface to the depth of 1.5 um at room temperature. Nanoindentation was performed to investigate the hardening behavior of the two materials under irradiation. It is found that the relation of maximum depth of plastic zone and indentation depth is not a fixed value. The maximum depth of plastic zone decreases with increase of damage level. Nix and Gao model was used to fit the measured hardness to obtain a hardness value H-o excluding indentation size effect (ISE), which can be used to characterize the hardening effect induced by irradiation. After fitting the data of H-o, it is found that there is an exponential relation between the H-o and damage level for both the V-4Ti and V materials. When the damage level is higher than similar to 0.2 dpa, the hardness increases slowly, this indicates a slow increase of pinning centers in samples at this damage level. Comparing the hardening fraction of V-4Ti and V samples, significant hardening can be seen for V sample, and it becomes severe especially at damage higher than similar to 0.2 dpa. The irradiation hardening resistance property of V-4Ti alloy is better than that of pure V. (C) 2015 Elsevier B.V. All rights reserved.
URL标识查看原文
WOS关键词DISPERSION-STRENGTHENED STEEL ; VANADIUM-BASE ALLOYS ; FE-CR ALLOYS ; MECHANICAL-PROPERTIES ; NEUTRON-IRRADIATION ; BEAM IRRADIATION ; INDENTATION ; BEHAVIOR ; REACTOR ; HELIUM
资助项目National Science Foundation of China[10975165]
WOS研究方向Materials Science ; Nuclear Science & Technology
语种英语
WOS记录号WOS:000350710700001
出版者ELSEVIER SCIENCE BV
源URL[http://ir.impcas.ac.cn/handle/113462/14978]  
专题近代物理研究所_能源材料研究组
近代物理研究所_材料研究中心
作者单位1.中国科学院近代物理研究所
2.中国科学院大学
推荐引用方式
GB/T 7714		 Song, Y,Yang, YT,Zhang, CH,et al. Nanoindentation on V-4Ti alloy irradiated by H and He ions[J]. JOURNAL OF NUCLEAR MATERIALS,2015,459(459):1-4.
APA Song, Y.,Yang, YT.,Zhang, CH.,Gou, J.,Liu, J.,...&Xian, YQ.(2015).Nanoindentation on V-4Ti alloy irradiated by H and He ions.JOURNAL OF NUCLEAR MATERIALS,459(459),1-4.
MLA Song, Y,et al."Nanoindentation on V-4Ti alloy irradiated by H and He ions".JOURNAL OF NUCLEAR MATERIALS 459.459(2015):1-4.

入库方式： OAI收割

来源：近代物理研究所

浏览0
下载0
收藏0
其他版本

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。