载能离子辐照钢铁材料硬化效应研究
文献类型：学位论文
| 作者 | 张恒庆 |
| 答辩日期 | 2014-05 |
| 授予单位 | 中国科学院研究生院 |
| 授予地点 | 北京 |
| 导师 | 张崇宏 |
| 关键词 | Ods钢 He离子 重离子 辐照硬化 |
| 学位名称 | 硕士 |
| 学位专业 | 材料学 |
| 其他题名 | Irradiation hardening of ODS ferritic steels under helium implantation and heavy-ion irradiation |
| 英文摘要 | The present work investigates the irradiation hardening of ODS ferritic steels after multi-energy He-ion implantation, or energetic Bi-ion and Xe-ion irradiation, to get an understanding of dependence of irradiation-hardening on atomic displacement damage and gas accumulation. Three kinds of high-Cr ODS ferritic steels including the commercial MA956 (19Cr-3.5Al), the 16Cr-0.1Ti and the 16Cr-0.1Zr ODS ferritic steels wereused. The results show that the hardness increases rapidly at the lower doses but tends to saturate at the higher dose. An 1/2-power law dependence on dpa value is obtained. Helium implantation contributes significantly to the irradiation hardening, possibly due to the impediment of the motion dislocations by helium bubbles.16Cr-ODS (Ti or Zr added) steels which contains finer oxide particles in higher number density show higher resistance to irradiation hardening than the MA956. |
| 源URL | [http://ir.impcas.ac.cn/handle/113462/17608]  |
| 专题 | 近代物理研究所_先进核能材料研究室（ADS） 近代物理研究所_能源材料研究组 |
| 作者单位 | 中国科学院近代物理研究所 |
| 推荐引用方式 GB/T 7714 | 张恒庆. 载能离子辐照钢铁材料硬化效应研究[D]. 北京. 中国科学院研究生院. 2014. |
入库方式： OAI收割
来源：近代物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。